相关论文: Evolution of magnetic and microstructural properti…

Chromium thin films deposited on silicon substrates by DC magnetron sputtering were systematically investigated as a function of film thickness, using a DC power of 50 W and a post-deposition annealing temperature of 200 C. Two types of…

Al2O3 thin films have been deposited at substrate temperatures between 500{\deg}C to 600{\deg}C by reactive magnetron sputtering using an additional arbitrary substrate bias to tailor the energy distribution of the incident ions. The films…

We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…

Nanoindentation tests were performed at several temperatures (24 to 80degC) on one antiwear zinc dialkyl-dithiophosphate (ZDTP) tribofilm using a Nanoindenter XP (R) entirely set into a climatic chamber. Mechanical properties of the…

Homogeneous freestanding films have been obtained by the direct current (DC) magnetron sputtering technique using a sacrificial layer. After annealing, the films are crystallized with a strong out-of-plane texture along the (022) direction.…

Biaxially textured LuNi2BC thin films with Tc up to 15.8 K and a residual resistivity ratio up to 15 have been prepared. The films were deposited on MgO(110) substrates using pulsed laser deposition from a stoichiometric target. Via the…

The structure, morphology, and electrical properties of epitaxial a-axis oriented thin films of Nd(0.2)Sr(0.8)MnO(3) are reported for thicknesses 10 nm <= t <= 150 nm. Films were grown with both tensile and compressive strain on various…

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…

Soft ferromagnetic NiFe thin films are promising for applications in spintronic devices because of their constituent electrical and magnetic properties. Electron beam evaporation and sputtering techniques have been used to deposit NiFe thin…

We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…

Superconducting Nb3Sn films were fabricated on sapphire and fine grain Nb substrates by magnetron sputtering from a single stoichiometric Nb3Sn target. The structural, morphological and superconducting properties of the films annealed for…

A series of MgB2 thin films were fabricated by pulsed laser deposition (PLD), doped with various amounts of Si up to a level of 18wt%. Si was introduced into the PLD MgB2 films by sequential ablation of a stoichiometric MgB2 target and a Si…

The dielectric properties of NiO thin films grown by pulsed laser deposition have been studied as a function of strain at temperature from 10 to 300 K. Above 150 K, the contribution of space-charge polarization to the dielectric…

Raman studies of nanocomposite SiCN thin film by sputtering showed that with an increase of substrate temperature from room temperature to 500oC, a transition from mostly sp2 graphitic phase to sp3 carbon took place which was observed from…

We report on the synthesis and characterization of nanocrystalline delta-MoN by crystallization of amorphous thin films grown on (100) Si by reactive sputtering at room temperature. Films with chemical composition MoN were grown using a…

We use room temperature ion beam assisted sputtering (IBAS) to deposit niobium nitride thin films. Electrical and structural characterizations were performed by electric transport and magnetization measurements at variable temperatures,…

A Li-Al-O thin film materials library, deposited by inert magnetron sputtering and post-deposition annealing in O2 atmosphere, was used to study the effects of different annealing temperatures (300 to 850{\deg}C) and durations (1 min to 7…

In this work, we studied cobalt nitride (Co-N) thin films deposited using a dc magnetron sputtering method at a substrate temperature (\Ts) of 523\,K. We find that independent of the reactive gas flow (\pn) used during sputtering, the…

High-dielectric-constant CaCu3Ti4O12 (CCTO) thin films were prepared on Pt/Ti/SiO2/Si(100) substrates by pulsed-laser deposition. The 480 nm thick polycrystalline films have preferred orientation and show obvious crystallization on the…

Perpendicular magnetic materials with low damping constant and high thermal stability have great potential for realizing high-density, non-volatile, and low-power consumption spintronic devices, which can sustain operation reliability for…