相关论文: Controlling Mn Depth Profiles in GaMnAs During Hig…
Mn concentration depth profiles in Mn-doped GaAs thin films grown at substrate temperatures of 580 and 250 {\deg}C using various Mn cell temperatures have been investigated with dynamic secondary ion mass spectrometry and Auger electron…
Mn doped GaAs thin films were grown using molecular beam epitaxy at high and low substrate temperatures. The elemental concentration depth profiles in the thin films were determined by using Auger electron spectroscopy combined with ion…
GaMnAs thin films with different Mn doping concentrations were grown via molecular beam epitaxy using a substrate temperature of 250 {\deg}C. The thin films were investigated using photoluminescence (PL) measurements from 8 to 300 K.…
We have studied the magneto-optical and magnetotrasnport properties of GaMnAs thin films with high Mn concentrations (x= 12.2 - 21.3%) grown by molecular-beam epitaxy. These heavily Mn-doped GaMnAs films were formed by decreasing the growth…
We have grown the ferromagnetic semiconductor GaMnAs containing up to 10% Mn by migration enhanced epitaxy at a substrate temperature of 150^oC. The alternate supply of As2 molecules and Ga and Mn atoms made it possible to grow single…
Single-phase Ni0.46Mn0.54As films with strained C1b symmetry have been successfully grown on GaAs (001) substrates by molecular-beam epitaxy. The epitaxial relationship between the film and the substrate has been studied using synchrotron…
GaMnAs/GaAs films were grown via molecular beam epitaxy using both low and high substrate temperatures. The films were investigated using Hall effect and photoluminescence (PL) measurements from 8 to 300 K. The carrier concentrations in the…
We report on the structural and magnetic properties of thin Ge(1-x)Mn(x)films grown by molecular beam epitaxy (MBE) on Ge(001) substrates at temperatures (Tg) ranging from 80deg C to 200deg C, with average Mn contents between 1 % and 11 %.…
Remarkably big increase of the substrate temperature during the low-temperature MBE growth of GaMnAs layers is observed by means of band gap spectroscopy. It is explained and simulated in terms of changes in the absorption/emission…
We report epitaxial growth and characterization of GaN thin films on sapphire (0001) substrates using low temperature GaN intermediate layer by plasma assisted molecular beam epitaxy (PA-MBE) technique. As grown and annealed GaN thin films…
We have performed an $in$-$situ$ depth profile study of Mn-doped GaN prepared by a low temperature thermal diffusion method using photoemission and x-ray absorption spectroscopy. It was revealed from the core-level photoemission…
In1-xMnxAs diluted magnetic semiconductor (DMS) thin films have been grown using metalorganic vapor phase epitaxy (MOVPE). Tricarbonyl(methylcyclopentadienyl)manganese was used as the Mn source. Nominally single-phase, epitaxial films were…
The use of highly efficient and solarblind GaN photocathodes as part of multichannel plate UV detectors for applications in astronomy would strongly benefit from the direct growth of GaN on typical window materials with high transmission…
A range of high quality Ga1-xMnxN layers have been grown by molecular beam epitaxy with manganese concentration 0.2 < x < 10%, having the x value tuned by changing the growth temperature (Tg) between 700 and 590 {\deg}C, respectively. We…
Mn-doped GaAs nanowires were grown in the self-catalytic growth mode on oxidized Si(100) surface by molecular beam epitaxy and characterized by scanning and transmission electron microscopy, Raman scattering, photoluminescence,…
Thin GaMnAs layers grown by molecular beam epitaxy were subjected to low-temperature post growth annealing, with an amorphous arsenic capping layer deposited on the GaMnAs surface directly after the epitaxial growth. It is shown that the…
Cubic (zinc-blende) Ga1-xMnxN layers were grown by plasma-assisted molecular beam epitaxy on GaAs (001) substrates. Some of the structures also contained cubic AlN buffer layers. Auger Electron Spectroscopy and Secondary Ion Mass…
The electrical and magnetic properties of p-type cubic (Ga,Mn)N thin films grown by plasma-assisted molecular beam epitaxy are reported. Hole concentrations in excess of 1018 cm-3 at room temperature are observed. Activated behaviour is…
We report on the magnetic and structural properties of Ar and Mn implanted InAs epitaxial films grown on GaAs (100) by Molecular Beam Epitaxy (MBE) and the effect of Rapid Thermal Annealing (RTA) for 30 seconds at 750C. Channeling Particle…
By employing a mixed SnO$_2$+Sn source, we demonstrate suboxide molecular beam epitaxy growth of phase-pure single crystalline metastable SnO(001) thin films at a growth rate of ~1.0nm/min without the need for additional oxygen. These films…