We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the…
Upper critical fields of four MgB2 thin films were measured up to 28 Tesla at Grenoble High Magnetic Field Laboratory. The films were grown by Pulsed Laser Deposition and showed critical temperatures ranging between 29.5 and 38.8 K and…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
Transition metal nitrides are a fascinating class of hard coating material that provide an excellent platform for investigating superconductivity and fundamental electron phonon interactions. In this work the structural morphological and…
We have measured the Raman spectra of polycrystalline MgB$_{2}$ from 25 {\cm} to 1200 {\cm}. When the temperature was decreased below the superconducting transition temperature $T_c$, we observed a superconductivity-induced redistribution…
We report resistivity and magnetization of single crystal MgB2, focusing on the broadening of superconducting (SC) transition in magnetic fields. In-plane and out-of-plane resistivity indicate that the broadening of superconducting…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
Two dimensional (2D) superconductivity was studied by magnetotransport measurements on single-atomic-layer Pb films on a cleaved GaAs(110) surface. The superconducting transition temperature shows only a weak dependence on the parallel…
Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…
In order to increase the accelerating gradient of Superconducting Radio Frequency (SRF) cavities, Magnesium Diboride (MgB2) opens up hope because of its high transition temperature and potential for low surface resistance in the high RF…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of…
We report and analyze reversible magnetization measurements on a high quality MgB2 single crystal in the vicinity of the zero field transition temperature, T_c=38.83 K, at several magnetic fields up to 300 Oe, applied along the c-axis.…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
The superconducting and structural properties of a series of Mg1-xAlxB2 samples have been investigated. X-ray diffraction results confirmed the existence of a structural transition associated with the significant change in inter-boron layer…
We report on study of the electronic anisotropy of the newly discovered MgB2 superconductor using the in-plane resistivity measurements in magnetic field applied perpendicular and parallel to Mg and B planes of MgB2 single crystals. The…
Magneto-resistivity of a c-axis oriented MgB$_{2}$ thin film was studied in perpendicular and parallel magnetic fields up to $\sim $23 T with temperatures down to 0.38 K. Resistive critical magnetic fields were determined. Large separations…