相关论文: Thermally-Activated Epitaxy of NbO

NbN films are grown on c-plane sapphire substrates by molecular beam epitaxy. The structural and superconducting properties of the film are characterized to demonstrate that growth parameters such as substrate temperature and active…

High temperatures promote kinetic processes which can drive crystal synthesis towards ideal thermodynamic conditions, thereby realizing samples of superior quality. While accessing very high temperatures in thin-film epitaxy is becoming…

We report molecular beam epitaxy synthesis of vacancy-ordered rocksalt NbO thin films which display superconductivity. A comparative study of substrates identifies Al$_2$O$_3$ (0001) as the optimal platform for realizing high-quality,…

The role of stoichiometry and growth temperature in the preferential nucleation of material phases in the Li-Nb-O family are explored yielding an empirical growth phase diagram. It is shown that while single parameter variation often…

By employing a mixed SnO$_2$+Sn source, we demonstrate suboxide molecular beam epitaxy growth of phase-pure single crystalline metastable SnO(001) thin films at a growth rate of ~1.0nm/min without the need for additional oxygen. These films…

In this work, we report on the growth of high-mobility $\beta$-Ga$_2$O$_3$ homoepitaxial thin films grown at a temperature much lower than the conventional growth temperature window for metalorganic vapor phase epitaxy. Low-temperature…

The growth of atomically-flat thin films of ferroelectric PbTiO3 on SrTiO3 substrates, using molecular beam epitaxy, is reported. The main issue in the growth of these materials is the high volatility of lead. This can be largely overcome…

Epitaxial NbO2 (110) films, 20 nm thick, were grown by pulsed laser deposition on Al2O3 (0001) substrates. The Ar/O2 total pressure during growth was varied to demonstrate the gradual transformation between NbO2 and Nb2O5 phases, which was…

Nb-doped SrTiO$_{3}$ epitaxial thin films have been prepared on (001) SrTiO$_{3}$ substrates using pulsed laser deposition. A high substrate temperature ($>1000^{\circ}{C}$) was found to be necessary to achieve 2-dimensional growth. Atomic…

We demonstrate the epitaxial growth of EuO on GaAs by reactive molecular beam epitaxy. Thin films are grown in an adsorption-controlled regime with the aid of an MgO diffusion barrier. Despite the large lattice mismatch, it is shown that…

NiO layers were grown on MgO(100), MgO(110), and MgO(111) substrates by plasma-assisted molecular beam epitaxy under Ni-flux limited growth conditions. Single crystalline growth with a cube-on-cube epitaxial relationship was confirmed by…

An epitaxial NdFeAs(O,F) thin film of 90 nm thickness grown by molecular beam epitaxy on MgO single crystal with Tc = 44.2 K has been investigated regarding a possible vortex glass-liquid tran-sition. The voltage-current characteristics…

Epitaxial films of NdFeAsO were grown on GaAs substrates by molecular beam epitaxy (MBE). All elements including oxygen were supplied from solid sources using Knudsen cells. The x-ray diffraction pattern of the film prepared with the…

Accessing unexplored conditions in crystal growth often reveals remarkable surprises and new regimes of physical behavior. In this work, performing molecular beam epitaxy of the technologically important superconductor NbN at temperatures…

Mn doped GaAs thin films were grown using molecular beam epitaxy at high and low substrate temperatures. The elemental concentration depth profiles in the thin films were determined by using Auger electron spectroscopy combined with ion…

We have fabricated Na_xCoO_2 thin films via lateral diffusion of sodium into Co_3O_4 (111) epitaxial films (reactive solid-phase epitaxy: Ref. 4). The environment of thermal diffusion is key to the control of the sodium content in thin…

NiO is a promising p-type material for photovoltaics and power electronics, but its temperature limits remain unclear. Using in situ high-temperature X-ray diffraction (HT-XRD) from 30 to 1100 C, we track the structural evolution of NiO…

Epitaxial films including bulk-like cubic and wurtzite polymorphs of MnSb have been grown by molecular beam epitaxy on GaAs via careful control of the Sb4/Mn flux ratio. Nonzero-temperature density functional theory was used to predict ab…

The electrical and magnetic properties of p-type cubic (Ga,Mn)N thin films grown by plasma-assisted molecular beam epitaxy are reported. Hole concentrations in excess of 1018 cm-3 at room temperature are observed. Activated behaviour is…

We report the growth of thin films of the mixed valence compound YbAl$_{3}$ on MgO using molecular-beam epitaxy. Employing an aluminum buffer layer, epitaxial (001) films can be grown with sub-nm surface roughness. Using x-ray diffraction,…