We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…

We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses…

A thin film technology compatible with multilayer device fabrication is critical for exploring the potential of the 39-K superconductor magnesium diboride for superconducting electronics. Using a Hybrid Physical-Chemical Vapor Deposition…

We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…

Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…

We have studied thermodynamics of the Mg-B system with the modeling technique CALPHAD using a computerized optimization procedure. Temperature-composition, pressure-composition, and pressure-temperature phase diagrams under different…

Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…

The effect of vacuum annealing thin films of the compensated ferrimagnetic half-metal Mn2RuxGa at temperatures from 250 to 400 degree Celsius is investigated. The 39.3 nm films deposited on (100) MgO substrates exhibit perpendicular…

Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…

The growth mechanisms of MgB2 films obtained by different methods on various substrates are compared via a detailed cross-sectional scanning electron microscopy (SEM) study. The analyzed films include (a) samples obtained by an ex-situ…

Very thick, ~ 40 $\mu$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The…

Superconducting magnesium diboride films with Tc0 ~ 24 K and sharp transition \~ 1 K were successfully prepared on silicon substrates by pulsed laser deposition from a stoichiometric MgB2 target. Contrary to previous reports, anneals at 630…

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…

We present a study on the power dependence of the microwave surface impedance in thin films of the novel superconductor MgB2. 500 nm thick samples exhibiting critical temperatures ranging between 26 and 38 K are synthesized by an ex-situ…

The electronic anisotropy in MgB2, is still a not completely clear topic; high quality c-oriented films are suitable systems to investigate this property. In this work we present our results on MgB2 superconducting thin films grown on MgO…

Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The…

We have successfully synthesized MgB2 thick films on 4H-SiC substrate by hybrid physical-chemical deposition (HPCVD). The films have transition temperature TC above 40 K. X-ray diffraction (XRD) shows the c-axis oriented structure of MgB2,…

In this paper we report a new sol-gel method for the fabrication of MgB2 films. Polycrystalline MgB2 films were prepared by spin-coating a precursor solution of Mg(BH_4)_2 diethyl ether on (001)Al2O3 substrates followed with annealing in Mg…

MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100)…

Growth of MgB2 thin films by pulsed laser deposition is examined under ex situ and in situ processing conditions. For the ex situ process, Boron films grown by PLD were annealed at 900 C with excess Mg. For the in situ process, different…