We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
The thermal stability of MgB2 has been studied experimentally to determine the role of thermodynamic and kinetic barriers in the decomposition process. The MgB2 decomposition rate approaches one monolayer per second at 650 C and has an…
Formation of MgB2 by reactions of Mg with B6Si and Mg with B were compared, the former also producing Mg2Si as a major product. Compared to the binary system, the ternary reactions for identical time and temperature were more complete at…
We present a study on the power dependence of the microwave surface impedance in thin films of the novel superconductor MgB2. 500 nm thick samples exhibiting critical temperatures ranging between 26 and 38 K are synthesized by an ex-situ…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
We present a study of the electrodynamic response of MgB2 pellets and thin film samples exhibiting critical temperatures ranging between 26 and 38 K. We have performed accurate measurements of the surface impedance ZS =RS+iXS as a function…
MgB2 thin films were deposited on SiC buffered Si substrates by sequential electron beam evaporation of B-Mg bilayer followed by in-situ annealing. The application of a SiC buffer layer enables the maximum annealing temperature of 830 C.…
The new superconductor MgB2 may prove useful for microwave applications at intermediate temperatures. MgB2 films with the thickness of 300 - 400 nm have surface resistance Rs less than 0.01 mOhms at a frequency (f) of 8.5 GHz and 7 K,and ~…
The microwave surface resistance Rs of MgB2 films with the zero-resistance temperature of - 39 K was measured at 8.0 - 8.5 GHz. The MgB2 films were prepared by deposition of boron films on c-cut sapphire, followed by annealing in a…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
Magnesium diboride (MgB2) thin films are a potential alternative to low-temperature superconductors (LTS) due to a higher critical temperature (Tc) of approximately 39 K. The reactive evaporation deposition technique also affords relatively…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…
Two issues related to the microwave surface impedance Z_s of MgB_2 thin film are discussed in this Letter, both being significant for potential microwave applications. At first, a correlation between Zs and Alpha = Xi/l was found, where Xi…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…
We have investigated the thermodynamic and kinetic barriers involved in the synthesis of MgB2 films. This work refines our initial conjectures predicting optimal MgB2 thin film growth conditions as a consequence of the unusually large…
The effects of Mg deficiency in MgB2 films grown by using hybrid physical-chemical vapor deposition were investigated after vacuum annealing at various temperatures. High-quality MgB2 films grown on c-cut Al2O3 substrates with different…