相关论文: Optical studies of charge dynamics in c-axis orien…
We investigated a high-quality MgB$_{2}$ thin film with a thickness of $\sim$1000 nm on an Al$_{2}$O$_{3}$ substrate using optical spectroscopy. We measured the reflectance spectra of the film at various temperatures both below, and above,…
The complex conductivity of a MgB2 film has been investigated in the frequency range 4 cm^{-1}< nu < 30 cm^{-1} and for temperatures 2.7 K < T <300 K. The overall temperature dependence of both components of the complex conductivity is…
Recent optical studies in c-axis oriented superconducting MgB$_2$ films indicate that the electron-phonon coupling is weak [tu01]. We reinforce this conclusion by examining the raw reflectance data; its frequency dependence is incompatible…
The optical conductivity of MgB$_2$ has been determined on a dense polycrystalline sample in the spectral range 6 meV - 4.6 eV using a combination of ellipsometric and normal incidence reflectivity measurements. $\sigma_{1}(\omega)$…
The anisotropic conductivity of thin Nd$_{1.85}$Ce$_{0.15}$CuO$_{4-\delta}$ films was measured in the frequency range 8 cm$^{-1}<\nu <$ 40 cm$^{-1}$ and for temperatures 4 K $<T<300$ K. A tilted sample geometry allowed to extract both,…
We have measured the reflectivity spectra of the iron based superconductor LiFeAs (Tc = 17.6 K) in the temperature range from 4 to 300 K. In the superconducting state (T < Tc), the clear opening of the optical absorption gap was observed…
Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…
We report the first study of the optical conductivity of MgB2 covering the range of its superconducting energy gap. Terahertz time-domain spectroscopy is utilized to determine the complex, frequency-dependent conductivity of thin films. The…
High-quality epitaxial MgB2 thin films prepared by pulsed laser deposition with Tc = 39 K offer the opportunity to study the anisotropy and robustness of the superconducting state in magnetic fields. We measure the in-plane electrical…
The ab-plane thermal conductivity $\kappa$ of single-crystalline hexagonal MgB_2 has been measured as a function of magnetic field H with orientations both parallel and perpendicular to the c-axis and at temperatures between 0.5 and 300 K.…
The temperature dependence of the real part of the microwave complex conductivity at 17.9 GHz obtained from surface impedance measurements of two c-axis oriented MgB2 thin films reveals a pronounced maximum at a temperature around 0.6 times…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…
Temperature-dependent reflectivity measurements in the frequency range 85 - 7000 cm$^{-1}$ were performed on BaFe$_2$As$_2$ single crystals under pressure up to $\sim$5 GPa. The corresponding pressure- and temperature-dependent optical…
Upper critical fields of four MgB2 thin films were measured up to 28 Tesla at Grenoble High Magnetic Field Laboratory. The films were grown by Pulsed Laser Deposition and showed critical temperatures ranging between 29.5 and 38.8 K and…
We have performed high-resolution photoemission spectroscopy on MgB2 and observed opening of a superconducting gap with a narrow coherent peak. We found that the superconducting gap is s-like with the gap value of 4.5 meV at 15 K. The…
In this paper, we analyze the upper critical field of four MgB2 thin films, with different resistivity (between 5 to 50 mWcm) and critical temperature (between 29.5 to 38.8 K), measured up to 28 Tesla. In the perpendicular direction the…
In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…
The conductivity and permittivity optical spectra of iron-pnictide Ba(Fe0.9Co0.1)2As2 film (Tc=20 K) are analyzed. In the superconducting state, at all temperatures up to Tc the temperature dependences of the magnetic field penetration…
The specific heat C of a sintered polycrystalline sample of MgB2 with a bulk superconducting transition temperature Tc=36.7 K is measured as a function of the temperature (2-300 K) and magnetic field (0-16 T), together with magnetic…
An important predicted, but so far uncharacterized, property of the new superconductor MgB2 is electronic anisotropy arising from its layered crystal structure. Here we report on three c-axis oriented thin films, showing that the upper…