We report on structural, magnetic, conductivity, and thermodynamic studies of FeSe$_{0.5}$Te$_{0.5}$ single crystals grown by self-flux and Bridgman methods. The samples were prepared from starting materials of different purity at various…
Single crystals of FeSe_1-x_Te_x_ (0.5=<x=<1) have been grown by the Bridgman method. After annealing them at 400 deg for 100 h in vacuum, single crystals of x=0.5-0.9 have exhibited bulk superconductivity. Anisotropic properties of the…
The magnetic moment in the superconducting and normal state of a crystalline FeTe0.65Se0.35 superconductor, grown by the Bridgman's method with relatively high growth rate, was measured. The temperature and magnetic field dependences of…
High quality single crystals of heavy Fermion CeCoIn5 superconductor have been grown by flux method with a typical size of (1~2)mm x (1~2)mm x ~0.1 mm. The single crystals are characterized by structural analysis from X-ray diffraction and…
Resistivity, magnetic susceptibility and heat capacity measurements are reported for single crystals of Fe1+yTexSe1-x grown via a modified Bridgeman method with 0 < y < 0.15, and x= 1, 0.9, 0.75, 0. 67, 0.55 and 0.5. Although resistivity…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition…
We report flux free growth of superconducting FeSe single crystals by an easy and versatile high temperature melt and slow cooling method for first time. The room temperature XRD on the surface of the piece of such obtained crystals showed…
We report successful growth of flux free large single crystals of superconducting FeSe1/2Te1/2 with typical dimensions of up to few cm. The AC and DC magnetic measurements revealed the superconducting transition temperature (Tc) value of…
Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline…
Here, we report self flux single crystal growth of FeTe1-xSex for x = 0 to 0.50 series via solid state reaction route,the resulted crystals as seen are shiny. X Ray diffraction performed on the surface of crystals elucidated the growth in…
High-quality and sizable single crystals are crucial for studying the intrinsic properties of unconventional superconductors, which are lacking in the 1111 phase of the Fe-based superconductors. Here we report the successful growth of…
The electronic specific heat of as-grown and annealed single-crystals of FeSe1-xTex (0.6<=x<=1) has been investigated. It has been found that annealed single-crystals with x=0.6-0.9 exhibit bulk superconductivity with a clear specific-heat…
Superconducting single crystals of SmFeAsO$_{1-x}$ without fluorine doping were grown at a pressure of 3.3 GPa and a temperature of 1350-1450 $^\circ$C by using the self-flux method. Plate-like single crystals of a few-150 $\mu$m in their…
We report the growth and characterization of single crystals of iron chalcogenide superconductor FeCr$_{0.02}$Se. There is an enhancement of the superconducting transition temperature (T$_{\rm c}$) as compared to the T$_{\rm c}$ of the…
Single crystalline FeTe$_{0.61}$Se$_{0.39}$ with a sharp superconducting transition at $T_{\textrm{c}} \sim$ 14 K is synthesized via slow furnace cooling followed by low-temperature annealing. The effect of annealing on the chemical and…
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l)…
Single crystals of tetragonal Fe1.00Se were grown from polycrystalline material by chemical vapor transport reaction at temperatures below 723 K using AlCl3 as transport additive. The plate-shaped single crystals have edge lengths up to 4…
The thermoelectric properties between 10 and 300 K and the growth of single crystals of n-type and p-type GeBi4Te7, GeSb4Te7, and the Ge(Bi1-xSbx)4Te7 solid solution are reported. Single crystals were grown by the modified Bridgman method,…
Single crystals of SmFeAsO1-xFy of a size up to 120 micrometers have been grown from NaCl/KCl flux at a pressure of 30 kbar and temperature of 1350-1450 C using the cubic anvil high-pressure technique. The superconducting transition…
High-quality Bi$_{2+x}$Sr$_{2-x}$CuO$_{6+\delta}$(0$<$x$\leq$0.5) single crystals have been grown successfully using the travelling-solvent floating-zone(TSFZ) technique. The samples with $x >$ 0.05 are in the underdoped level. The…