相关论文: A sol-gel method for growing superconducting MgB2 …

Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…

Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…

We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…

ctical superconducting material for power-electric products such as superconducing tapes because of its high superconducting transition temperature (Tc) of 39 K and its high critical current density (Jc) under magnetic fields.…

The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…

Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…

We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses…

Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…

Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and…

We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…

Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…

We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…

A Hybrid Physical-Chemical Vapour Deposition (HPCVD) system consisting of separately controlled Mg-source heater and substrate heater is used to grow MgB2 thin films and thick films at various temperatures. We are able to grow…

MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…

The growth mechanisms of MgB2 films obtained by different methods on various substrates are compared via a detailed cross-sectional scanning electron microscopy (SEM) study. The analyzed films include (a) samples obtained by an ex-situ…

A complexing molecule electrodeposition technique has been developed for the deposition of low cost, lightweight MgB2 films, for the first time. Different deposition parameters such as bath composition, deposition potential, current…

Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…

Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained…

Very thick, ~ 40 $\mu$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The…