The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…

High quality MgB2 thin films have been obtained by pulsed laser deposition both on MgO and on Al2O3 substrates using different methods. In the standard two-step procedure, an amorphous precursor layer is deposited at room temperature…

Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…

We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…

Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…

The electronic anisotropy in MgB2, is still a not completely clear topic; high quality c-oriented films are suitable systems to investigate this property. In this work we present our results on MgB2 superconducting thin films grown on MgO…

Growth of MgB2 thin films by pulsed laser deposition is examined under ex situ and in situ processing conditions. For the ex situ process, Boron films grown by PLD were annealed at 900 C with excess Mg. For the in situ process, different…

MgB2 thin films were deposited using Pulsed Laser Deposition (PLD) and ex-situ annealing in Mg atmosphere. The films presented critical temperatures up to 36K and turned out to be preferentially c-oriented both on Al2O3 (r-cut) and MgO(100)…

We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…

Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and…

We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…

Two types of MgB2 films were prepared by pulsed laser deposition (PLD) with in situ and ex situ annealing processes respectively. Significant differences in properties between the two types of films were found. The ex situ MgB2 film has a…

Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The…

MgB2 thin films were cold-grown on sapphire substrates by pulsed laser deposition (PLD), followed by post-annealing in mixed, reducing gas, Mg-rich, Zr gettered, environments. The films had Tcs in the range 29 K to 34 K, Jcs (20K, H=0) in…

We report the growth of high-quality epitaxial MgB2 thin films on (1102) Al2O3 and (001) SrTiO3 substrates by using a pulsed laser deposition technique. The thin films grown on Al2O3 substrates show a Tc of 39 K with a sharp transition…

A large anisotropy in the upper critical field (H$_{C2}$) is observed for MgB$_{2}$ films grown in situ by a pulsed laser deposition process involving growth and annealing of Mg and B multilayers. Measurements of resistivity as a function…

Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…

The electronic anisotropy in MgB2, which arises from its layered crystal structure is not completely clear until now. High quality c-oriented films offer the opportunity of studying such property. MgB2 thin films were deposited by using two…

Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained…

Superconducting magnesium diboride films with Tc0 ~ 24 K and sharp transition \~ 1 K were successfully prepared on silicon substrates by pulsed laser deposition from a stoichiometric MgB2 target. Contrary to previous reports, anneals at 630…