相关论文: Superconducting properties of MgB2 thin films prep…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
Superconducting thin films have been prepared in a two-step in-situ process, using the Mg-B plasma generated by pulsed laser ablation. The target was composed of a mixture of Mg and MgB2 powders to compensate for the volatility of Mg and…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
We introduce a simple method of an MgB2 film preparation using sequential electron-beam evaporation of B-Mg two-layer (followed by in-situ annealing) on the NbN buffered Si(100) substrate. The Transmission Electron Microscopy analyses…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
Thin films of MgB2 superconductor were prepared by three different procedures on sapphire and silicon substrates. Boron thin films, ex-situ annealed in magnesium vapour, resulted in textured polycrystalline films with crystal dimensions…
The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…
Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…
Superconducting thin films have been prepared on Si-substrates, using pulsed laser deposition from a target composed of a mixture of Mg and MgB2 powders. The films were deposited at room temperature and post-annealed at 600 degrees C. The…
MgB2 thin films were deposited on SiC buffered Si substrates by sequential electron beam evaporation of B-Mg bilayer followed by in-situ annealing. The application of a SiC buffer layer enables the maximum annealing temperature of 830 C.…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
As-grown superconducting thin films of MgB2 were prepared by molecular beam epitaxy (MBE), and studied by X-ray and ultraviolet photoelectron spectroscopy (XPS and UPS). Only films prepared at temperatures between 150 and 320 deg. showed…
Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…
Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
Ultrathin MgB2 superconducting films with a thickness down to 7.5 nm are epitaxially grown on (0001) Al2O3 substrate by hybrid physical-chemical vapor deposition method. The films are phase-pure, oxidation-free and continuous. The 7.5 nm…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…
We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…