The glass transition temperature $T_g$ and the temperature $T_{\alpha}$ corresponding to the peak in the dielectric loss due to the $\alpha$-process have been simultaneously determined as functions of film thickness $d$ through dielectric…
The glass transition temperature $T_{\rm g}$ and the temperature $T_{\alpha}$ corresponding to the peak in the dielectric loss due to the $\alpha$-process have been simultaneously determined as functions of film thickness d through…
The $\alpha$-process (segmental motion) of thin polystyrene films supported on glass substrate has been investigated in a wider frequency range from 10$^{-3}$ Hz to 10$^4$ Hz using dielectric relaxation spectroscopy and thermal expansion…
The glass transition temperature and relaxation dynamics of the segmental motions of thin films of polystyrene labeled with a dye, 4-[N-ethyl-N-(hydroxyethyl)]amino-4-nitraozobenzene (Disperse Red 1, DR1) are investigated using dielectric…
We investigate the relaxation behavior of thin films of a polyamide random copolymer, PA66/6I, with various film thicknesses using dielectric relaxation spectroscopy. Two dielectric signals are observed at high temperatures, the…
Dynamics of thin films of poly(vinyl acetate) (PVAc) and poly(methyl methacrylate) (PMMA) have been investigated by dielectric relaxation spectroscopy in the frequency range from 0.1Hz to 1MHz at temperatures from 263K to 423K. The…
Glass transition process gets affected in ultrathin films having thickness comparable to the size of the molecules. We observe systematic broadening of glass transition temperature (Tg) as the thickness of the polymer film reduces below the…
Recent experiments have demonstrated that the glass transition temperature of thin polymer films can be shifted as compared to the same polymer in the bulk, the amplitude and the sign of this effect depending on the interaction between the…
A non-contact scanning-probe-microscopy method was used to probe local near-surface dielectric susceptibility and dielectric relaxation in poly-vinyl-acetate (PVAc) near the glass transition. Dielectric spectra were measured from 10-4 Hz to…
In an earlier preprint (V. V. Ginzburg, O. V. Gendelman, R. Casalini, and A. Zaccone, arxiv:2409.17291), we demonstrated that the dynamic (relaxation time) and volume equations of state for many amorphous polymers are near-universal -- each…
The glass transition temperature and its connection to statistical properties of confined and free-standing polymer films of varying thickness containing unentangled to highly entangled bead-spring chains are studied by molecular dynamics…
The glass transition temperature ($T_g$) of polymer thin films has been a subject of controversy in the last two decades. (Pseudo)thermodynamic determinations of $T_g$ generally suggest a significant depression, whereas the molecular…
The viscoelastic properties of thin polymeric films represent a central issue, especially for nanotechnological applications. In particular, it is highly relevant the dependence of viscoelasticity on the temperature. For polystyrene it is…
Aging dynamics in thin films of poly(methyl methacrylate) (PMMA) have been investigated through dielectric measurements for different types of aging processes. The dielectric constant was found to decrease with increasing aging time at an…
A simple and predictive model is put forward explaining the experimentally observed substantial shift of the glass transition temperature, Tg, of sufficiently thin polymer films. It focuses on the limit of small molecular weight, where…
Understanding the temperature dependence of the optical properties of thin metal films is critical for designing practical devices for high temperature applications in a variety of research areas, including plasmonics and near-field…
The molecular mobility of glassy and supercooled liquid states of clotrimazole is studied using broadband dielectric spectroscopy for a wide range of temperatures and frequency. The dielectric loss data of clotrimazole below T$_{g}$, do not…
The temperature dependence of optical constants of titanium nitride thin film is investigated using spectroscopic ellipsometry between 1.4 to 5 eV in the temperature range 300 K to 650 K in steps of 50 K. The real and imaginary parts of the…
We have investigated the reduction of the glass transition temperature, $T_g$, for thin supported films of particularly small molecular weight ($M_W$ = 2 kg/mol) polystyrene, and found good agreement with earlier studies on larger…
The glass transition in amorphous poly(ethylene terephthalate) is studied by thermally stimulated depolarization currents (TSDC) and differential scanning calorimetry (DSC). The ability of TSDC to decompose a distributed relaxation, as the…