We demonstrate low loss ridge waveguides and the first ring resonators for the mid-infrared, for wavelengths ranging from 5.4 to 5.6 {\mu}m. Structures were fabricated using electron-beam lithography on the silicon-on-sapphire material…
In this paper we report suspended silicon waveguides operating at a wavelength of 7.67 mm with a propagation loss of 3.1 ? 0.3 dB/cm. To our knowledge this is the first demonstration of low loss silicon waveguides at such a long wavelength,…
Broadband mid-infrared light sources are highly desired for wide-ranging applications that span free-space communications to spectroscopy. In recent years, silicon has attracted great interest as a platform for nonlinear optical wavelength…
Broadband mid-infrared (mid-IR) spectroscopy applications could greatly benefit from today's well-developed, highly scalable silicon photonics technology; however, this platform lacks broadband transparency due to its reliance on absorptive…
It has recently been shown that silicon nanophotonic waveguides can be used to construct all of the components of a photonic data transmission system on a single chip. These components can be integrated together with CMOS electronics to…
Novel photonic nanowires were fabricated using low-index materials and tested in the near-infrared spectrum to assess their nonlinear optical properties. In this work, we argue the need to redefine the standard nonlinear figure of merit in…
Periodically poled thin-film lithium niobate (TFLN) waveguides have emerged as a leading platform for highly efficient frequency conversion in the near-infrared. However, the commonly used silica bottom-cladding results in high absorption…
In this paper, we demonstrate the integration of photonic devices on sapphire substrates using multi-layer depressed cladding waveguides at both 780 nm and 1550 nm. The devices are up to 10-cm long and written at depths down to 400 um. The…
Sapphire is a promising wideband substrate material for visible photonics. It is a common growth substrate for III-nitride light-emitting diodes and laser structures. Doped sapphires are important gain media foundational to the development…
Nanophotonic waveguides with sub-wavelength mode confinement and engineered dispersion profiles are an excellent platform for application-tailored nonlinear optical interactions at low pulse energies. Here, we present fully air clad…
In this work, we demonstrate compact paper-clip spiral silicon photonic waveguides with ultra-low delay loss. We characterize the optical loss and group delay of single-mode and multi-mode silicon waveguides across the telecom O-, S-, C-,…
We fabricate and characterize waveguides composed of closely spaced and longitudinally oriented silicon ridges etched into silicon-on-insulator wafers. Through both guided mode and bulk measurements, we demonstrate that the patterning of…
Superconducting nanowire single-photon detectors are widely used for detecting individual photons across various wavelengths from ultraviolet to near-infrared range. Recently, there has been increasing interest in enhancing their…
The microscale integration of mid- and longwave-infrared photonics could enable the development of fieldable, robust chemical sensors, as well as highly efficient infrared frequency converters. However, such technology would be defined by…
A mid-infrared single photon detector (MIR-SNSPD) was reported based on 30 nm-wide superconductor molybdenum silicide nanowires in this work. Saturated quantum efficiencies (QEs) were achieved at the wavelength ranging from 1.55 to 5.07…
Silicon photonics is being extended from the near-infrared (near-IR) window of 1.3-1.5 {\mu}m for optical fiber communications to the mid-infrared (mid-IR) wavelength-band of 2 {\mu}m or longer for satisfying the increasing demands in many…
The need for semiconductor technology for crystalline silicon of the highest purity and homogeneity has provided samples exhibiting low optical absorption in the infrared range. Such silicon has become the basis for photonic elements in the…
We show that subwavelength silicon-rich nitride waveguides efficiently sustain high-speed transmissions at 2 $\mu$m. We report the transmission of a 10 Gbit/s signal over 3.5 cm with negligible power penalty. Parametric conversion in the…
We demonstrate for the first time a mid infrared silicon Raman amplifier. Amplification of 12 dB is reported for a signal at 3.39 micron wavelength. The active medium was a 2.5 cm long silicon sample that was pumped with 5ns pulses at 2.88…
A first demonstration and complete characterization of mid-infrared waveguides in diamond are reported in detail. Waveguides were designed for 2.4 um and 8.6 um waveguiding, with their group velocity dispersion was analyzed using…