Pure as well as Ag- and Au-substituted YbInCu$_4$ single crystals were structurally and chemically characterized and investigated by means of heat capacity, magnetization, resistivity and ultrasonic measurements. We studied the influence of…
Single crystals of EuPd2Sb2 have been grown from PdSb self-flux. The properties of the single crystals have been investigated by x-ray diffraction, magnetic susceptibility chi, magnetization M, electrical resistivity rho, Hall coefficient…
Recent discovery of superconductivity in iron pnictides had attracted immense attention of the scientific community. The parent compounds were spin density wave (SDW) metals unlike the high-TC superconductors which were Mott insulators. In…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
We present magnetization, specific heat, and 27Al NMR investigations on YbFe2Al10 over a wide range in temperature and magnetic field. The magnetic susceptibility at low temperatures is strongly enhanced at weak magnetic fields, accompanied…
We report a combined experimental and theoretical study on intriguing magnetic properties of quasiferroelectric orthochromates. Large single crystals of the family of RECrO$_3$ (RE = Y, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu) compounds were…
We successfully synthesized two new compounds Rb$_x$Fe$_{2-y}$S$_2$ and Cs$_x$Fe$_{2-y}$S$_2$ which were isostructural with K$_x$Fe$_{2-y}$Se$_2$ superconductor. We systematically investigated the resistivity, magnetism and thermoelectric…
The intermediate valence compound YbAl3 exhibits a broad magnetic excitation with characteristic energy E1 ~ 50meV, of order of the Kondo energy (TK ~ 600-700K). In the low temperature (T < Tcoh ~ 40K) Fermi liquid state, however, a new…
We report the anisotropic magnetic properties of the ternary compound ErAl$_2$Ge$_2$. Single crystals of this compound were grown by high temperature solution growth technique,using Al:Ge eutectic composition as flux. From the powder x-ray…
We report on the single crystal growth of Eu(Pd$_{1-x}$Au$_x$)$_2$Si$_2$, $0< x\leq 0.2$, from a levitating Eu-rich melt using the Czochralski method. Our structural analysis of the samples confirms the ThCr$_2$Si$_2$-type structure as well…
Magnetic susceptibility, heat capacity, and electrical resistivity measurements have been carried out on single crystals of the intermediate valence compounds Yb2Rh3Ga9 and Yb2Ir3Ga9. These measurements reveal a large anisotropy due…
Single crystals of AlFe$_{2}$B$_{2}$ have been grown using the self flux growth method and then measured the structural properties, temperature and field dependent magnetization, and temperature dependent electrical resistivity at ambient…
We investigated the occurrence and nature of superconductivity in single crystals of YFe$_2$Ge$_2$ grown out of Sn flux by employing x-ray diffraction, electrical resistivity, and specific heat measurements. We found that the residual…
We report on the single crystal growth of the heavy-fermion compounds YbRh2Si2 and YbIr2Si2 using a high-temperature indium-flux technique. The optimization of the initial composition and the temperature-time profile lead to large (up to…
\alpha-Fe single crystals of rhombic dodecahedral habit were grown from a melt of Li$_{84}$N$_{12}$Fe$_{\sim 3}$. Crystals of several millimeter along a side form at temperatures around $T \approx 800^\circ$C. Upon further cooling the…
Single crystals of Cu$_{13}$Ba were successfully grown out of Ba-Cu self flux. Temperature dependent magnetization, $M(T)$, electrical resistivity, $\rho(T)$, and specific heat, $C_p(T)$, data are reported. Isothermal magnetization…
The preparation of mixed crystals of NaBr and KBr from melt as well as their physical characterization have been reported. Electrical measurements were carried out at various temperatures, which showed that their conductivity increases with…
The compound CaV2O4 contains V^{+3} cations with spin S = 1 and has an orthorhombic structure at room temperature containing zigzag chains of V atoms running along the c-axis. We have grown single crystals of CaV2O4 and report…
Using a new horizontal flux growth technique to produce high quality crystals of the unconventional superconductor YFe$_2$Ge$_2$ has led to a seven-fold reduction in disorder scattering, resulting in mm-sized crystals with residual…
We present results from point-contact spectroscopy of the antiferromagnetic heavy-fermion superconductor UPd$_2$Al$_3$: conductance spectra are taken from single crystals with two major surface orientations as a function of temperature and…