F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2…
R(O,F)BiS2 (R: La, Ce, Pr, Nd) superconducting single crystals with different F concentrations are grown using a CsCl/KCl flux. The obtained 1-2 mm-sized single crystals have a plate-like shape and are cleavable along the ab-plane. The…
F-substituted LaOBiSe2 single crystals were grown using CsCl flux. The obtained single crystals showed a plate-like shape with a size of about 1.0 mm square. The c-axis lattice constant of the grown crystals was determined to be 14.114(3)…
Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using…
Cd-doped La(O,F)BiS2 single crystals were grown using a CsCl/KCl flux. The grown crystals have a plate-like shape with ~1-2 mm square size in a well-developed ab-plane. The Cd doping in the crystals was successfully characterized by single…
"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the…
NbBiCh$_3$ (Ch = S, Se) misfit-layered superconducting single crystals were successfully grown using a CsCl/KCl flux for the first time. The obtained crystals had a well-developed habit parallel to the c-plane with a typical width of 1-2 mm…
(La,Ce)OBiS2 single crystals are successfully grown using CsCl flux. The obtained single crystals have a plate-like shape with a size of 0.5-2.0 mm and a well-developed ab-plane. The thickness of the crystals increases with a decrease in…
The BiS2-based superconductors were discovered recently. The superconductivity has been proved by many other groups. Since the previous experiments were all done on polycrystalline samples, therefore there remains a concern whether the…
Single crystal of La(O,F)BiSe2 was successfully grown for the first time by the CsCl flux method. Single crystal X-ray structural analysis clearly showed that La(O,F)BiSe2 crystalizes with space group P4/nmm (lattice parameters a =…
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated…
Single crystals of La(O,F)BiSSe were successfully grown by a CsCl flux method. Single crystal X-ray structural analysis revealed that the crystal structure is isostructural with BiS$_2$- or BiSe$_2$-based compounds with space group $P4/nmm$…
CsCa$_2$Fe$_4$As$_4$F$_2$ is a newly discovered iron-based superconductor with $T_\mathrm{c}\sim$ 30 K containing double Fe$_2$As$_2$ layers that are separated by insulating Ca$_2$F$_2$ spacer layers. Here we report the transport and…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…
Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The…
Sb- and Se-substituted CeOBiS2 single crystals have been successfully grown using CsCl/KCl flux. Sb and Se substitution dependence of the superconductivity on CeOBiS2 was investigated and the superconducting phase diagram at above 0.3 K was…
We present an optical spectroscopy study on F-substituted NdOBiS$_2$ superconducting single crystals grown using KCl/LiCl flux method. The measurement reveals a simple metallic response with a relatively low screened plasma edge near 5000…
F-doped LaOBiSe$_{2}$ superconducting single crystals with typical size of 2$\times$4$\times$0.2 mm$^{3}$ are successfully grown by flux method and the superconducting properties are studied. Both the superconducting transition temperature…
We investigate the superconducting properties and possible nematic superconductivity of self-doped BiCh2-based (Ch: S, Se) superconductor CeOBiS1.7Se0.3 through the measurements of in-plane anisotropy of magnetoresistance. Single crystals…
Single crystals of undoped CaFe2As2 were grown by a FeAs self-flux method, and the crystals were quenched in ice-water rapidly after high temperature growth. The quenched crystal undergoes a collapsed tetragonal structural phase transition…