Copper ferrite thin films were deposited on amorphous quartz substrates. The as deposited films were annealed in air and either quenched or slow cooled. Magnetization studies were carried out on the as deposited as well as annealed films…
Copper ferrite thin films were rf sputtered at a power of 50W. The as deposited films were annealed in air at 800{\deg}C and slow cooled. The transmission electron microscope (TEM) studies were carried out on as deposited as well as on slow…
We report on the magnetic properties of zinc ferrite thin film deposited on SrTiO$_3$ single crystal using pulsed laser deposition. X-ray diffraction result indicates the highly oriented single phase growth of the film along with the…
5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…
Ta (100 nm) / NdFeB (5 $\mu$m) / Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ~ 18 $\mu$m/h). A 2-step procedure was used : deposition at temperatures up to 400 C followed by ex-situ…
Thin films of the charge-ordered (CO) compound Pr$_{0.5}$Ca$_{0.5}$MnO$_{3}$ have been deposited onto (100)-oriented SrTiO$_{3}$ substrates using the Pulsed Laser Deposition technique. Magnetization and transport properties are measured…
The effect of vacuum annealing thin films of the compensated ferrimagnetic half-metal Mn2RuxGa at temperatures from 250 to 400 degree Celsius is investigated. The 39.3 nm films deposited on (100) MgO substrates exhibit perpendicular…
The magnetization (M) as a function of temperature (T) from 2 to 300 K and in-plane field (H) up to 1 kOe, room temperature easy and hard direction in-plane field hysteresis loops for fields between -100 and +100 Oe, and 10 GHz…
Copper oxide thin films are deposited on quartz substrates by DC magnetron sputtering and the effect of deposition temperature on their optoelectronic properties is examined in detail. Scanning Electron Microscopy (SEM), X-ray diffraction…
The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kAm-1, which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 muB that is…
Chromium thin films deposited on silicon substrates by DC magnetron sputtering were systematically investigated as a function of film thickness, using a DC power of 50 W and a post-deposition annealing temperature of 200 C. Two types of…
We report the deposition of thin Co$_2$FeSi films by RF magnetron sputtering. Epitaxial (100)-oriented and L2$_1$ ordered growth is observed for films grown on MgO(100) substrates. (110)-oriented films on Al$_2$O$_3$(110) show several…
5$\mu$m thick SmCo films were deposited onto Si substrates using triode sputtering. A study of the influence of deposition temperature (Tdep <= 600 degrees C) on the structural, magnetic and mechanical properties has shown that optimum…
The rf sputtered copper ferrite films contain nanocrystalline grains. In these films, the magnetization does not saturate even in high magnetic fields. This phenomenon of high field susceptibility is attributed to the defects and/or…
Varying the substrate temperature changes structural and magnetic properties of spinel ferrite NZFO thin films. XRD of films grown at different temperature display only 004 reflections, without any secondary peaks, showing growth…
We report on magnetron deposition of thin superconducting rhenium films on sapphire substrates. During the deposition, substrates were held at ambient temperature. Critical temperature of the films is Tc~3.6 K. Films have polycrystalline…
The linear magnetoelectric effect was measured in 500 nm Cr2O3 films grown by rf sputtering on Al2O3 substrates between top and bottom thin film Pt electrodes. Magnetoelectric susceptibility was measured directly by applying an AC electric…
We present a comparative study on the influence of applied magnetic field on the resistance of $C_{1-x}Co_x$ thin films (with $x=0.1$, $0.15$ and $0.2$) grown on $Si$ substrate by pulsed laser deposition technique. It is found that the…
Al-doped ZnO thin films were deposited using reactive high power impulse magnetron sputtering at substrate temperatures between room temperature and 600 $\bullet$ C. Two sample series with different oxygen partial pressures were studied.…
Magnetic properties of MnAs were studied as a function of temperature with a superconducting interference device (5 K to 350 K), and atomic force microscopy/magnetic force microscopy (20 K to 360 K). Structural and magnetic properties of…