Two sets of MgB2 samples doped with up to 5 at. % of Al were prepared in different laboratories using different procedures. Decreases in the a and c lattice parameters were observed with Al doping confirming Al substitution onto the Mg…
We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…
Magnesium diboride superconducting wires give the largest critical current density (Jc) when produced with iron sheath. Because iron is ferromagnetic, it is expected to improve the field dependence of Jc by shielding of the external field…
Improving transport current has been the primary issue for practical application of superconducting wires and tapes. However, the porous nature of powder-in-tube (PIT) processed iron-based superconducting tapes is thought to be one of the…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
The effect of doping MgB2 with carbon nanotubes on transition temperature, lattice parameters, critical current density and flux pinning was studied for MgB2-xCx with x = 0, 0.05, 0.1, 0.2 and 0.3. The carbon substitution for B was found to…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2…
We demonstrate a large enhancement of critical current density (Jc) up to 1.0x10^7 A/cm2 at 5 K under self-field in (Ba,K)Fe2As2 single crystals by irradiating 320 MeV Au ions. With the very promising potential of this material in mind, we…
Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires…
Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
A review of current developments in the study of chemical doping effect on the superconducting properties of MgB2 wires and tapes is presented, based on the known literature data and our own results. The critical current density of MgB2 can…
Bi-2212 is the only high-field, high-temperature superconductor (HTS) capable of reaching a critical current density $J_{\text{c}}$(16 T, 4.2 K) of 6500 $\mathrm{A\cdot mm^{-2}}$ in the highly desirable round wire (RW) form. However,…
The critical current density (Jc) of hot isostatic pressed (HIPed) MgB2 wires, measured by d.c. transport and magnetization, is compared with that of similar wires annealed at ambient pressure. The HIPed wires have a higher Jc than the…
Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of…
The high upper critical field and low anisotropy of iron-based superconductors make them being particularly attractive for high-field applications. However, the current carrying capability needs to be enhanced by overcoming the weak-link…
The effect of the quality of starting powders on the microstructure and superconducting properties of in-situ processed Fe-sheathed MgB2 tapes has been investigated. Three different types of commercial atomized spherical magnesium powder…