We address the effect of MgO impurity on the superconducting properties of MgB2. The synthesis of MgB2 is very crucial because of sensitivity of Mg to oxidation which may lead to MgO as a secondary phase. Rietveld refinement was performed…

In this paper we report a new sol-gel method for the fabrication of MgB2 films. Polycrystalline MgB2 films were prepared by spin-coating a precursor solution of Mg(BH_4)_2 diethyl ether on (001)Al2O3 substrates followed with annealing in Mg…

The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…

The discovery of superconductivity at 39 K in MgB2[1] raises many issues. One of the central questions is whether this new superconductor resembles a high-temperature-cuprate superconductor or a low-temperature metallic superconductor in…

Monofilamentary MgB2-wires with a 2- or 3-component sheath containing mechanical reinforcing stainless steel (SS) were prepared and characterized. In direct contact to the superconductor Nb, Ta or Fe was used. For a selection of samples…

The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…

Transport critical current densities and n-values were measured at 4.2 K in fields up to 15 T on 7, 19, and 37-stack multifilamentary MgB2 strands made using an in-situ route. Some strands included SiC additions (particle size 30 nm), while…

Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…

The use of MgB2 in superconducting applications still awaits for the development of a MgB2-based material where both current-carrying performance and critical magnetic field are optimized simultaneously. We achieved this by doping MgB2 with…

Superconducting at 40 K MgB2 -samples were obtained by direct reaction from elements in molybdenum crucibles under argon pressure. Pressure allows to provide annealing at temperature up to 1400oC, that resulting in rise of Tc and…

The DC magnetization and AC complex magnetic susceptibilities were measured for MgB2 single crystals, unsubstituted and carbon substituted with the composition of Mg(B_0.94C_0.06)2. The measurements were performed in AC and DC magnetic…

We synthesized polycrystalline MgB2 from a stoichiometric mixture of Mg and the 11 B isotope under different conditions. All the samples showed bulk superconductivity with Tc = 38~39 K. The samples containing the least amount of unreacted…

Nanocrystalline MgB$_2$ produced by mechanical alloying has been shown to exhibit enhanced superconducting properties such as increased pinning and higher critical currents. However, the effects of the synthesis process on the intrinsic…

A commercial stainless steel tube was employed to synthesize MgB2. The specimen was prepared by a stoichiometric mixture of Mg and B. The specimen that had been enveloped in the commercial stainless steel tube was synthesized for 2 hours at…

The effects of Mg deficiency in MgB2 films grown by using hybrid physical-chemical vapor deposition were investigated after vacuum annealing at various temperatures. High-quality MgB2 films grown on c-cut Al2O3 substrates with different…

The two most common types of MgB2 conductor fabrication technique - in-situ and ex-situ - show increasing conflicts concerning the connectivity, an effective current-carrying cross-sectional area. An in-situ reaction yields a strong…

Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…

We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…

Both hexagonal wurtzite and cubic zinc blend GaN phases were synthesized in GaAs by 50 keV N+ implantation at 400 deg C and subsequent annealing at 900 deg C for 15 min in N2 ambient. Crystallographic structural and Raman scattering studies…

Cold high pressure densification (CHPD) is presented as a new way to substantially enhance the critical current density of in situ MgB2 wires at 4.2 and 20 K at fields between 5 and 14 T. The results on two binary MgB2 wires and an alloyed…