Clear evidence of ferromagnetic behavior at temperatures >400 K as well as spin polarization of the charge carriers have been observed in ZnMnO thin films grown on Al2O3 and MgO substrates. The magnetic properties depended on the exact Mn…

The magnetization as a function of magnetic field showed hysteretic behavior at room temperature. According to the temperature dependence of the magnetization, the Curie temperature $(T_{C})$ is higher than 350 K. Ferromagnetic Mn-doped tin…

We observe remarkably strong room temperature ferromagnetism (~1.5 Bohr Magneton/Mn) in optically transparent Mn(II)-doped indium tin oxide (ITO) films. The nanocrystalline films with average grain size 10-22 nm and thickness 150-350 nm are…

Ferromagnetism above room temperature was observed in Cr-doped hydrogenated amorphous silicon films deposited by rf magnetron-sputtering. Structure analysis reveals that films are amorphous without any detectable precipitates up to the…

Magnetic properties of thin films differs from that of the corresponding bulk materials and show novel physics as a result of their reduced size and dimensionality. Profound changes in magnetic properties can also result with exchange bias…

Thin films grown by pulsed-laser deposition from targets of Sn0.95Fe0.05O2 are transparent ferromagnets with Curie temperature and spontaneous magnetization of 610 K and 2.2 Am2kg-1, respectively. The 57Fe Mossbauer spectra show the iron is…

Thin films of Ti1-xFexO2 (x=0 and 0.05) have been prepared on sapphire substrates by spin-on technique starting from metal organic precursors. When heat treated in air at 550 and 700 degrees C respectively, these films present pure anatase…

Temperature and fluence dependence of the transient photoinduced reflectivity and the magnetooptical Kerr angle was measured in two Pr0.6Ca0.4MnO3 thin films subject to tensile and compressive substrate-induced strain. A photoinduced…

We have investigated the magnetic properties of (Ga,Mn)As thin films with Mn concentration between 1 and 9%. Ferromagnetic transition temperatures TC of up to 173K are observed. The results are compared to the predictions of the Zener…

Thin films of Ti1-xCoxO2 (x=0 and 0.03) have been prepared on sapphire substrates by spin-on technique starting from metalorganic precursors. When heat treated in air at 550 and 700 C respectively, these films present pure anatase and…

The magnetization of a thin Fe-Co cyanide film has been investigated from 5 K to 300 K and in fields up to 500 G. Upon illumination with visible light, the magnetization of the film rapidly increases. The original cluster glass behavior is…

Occurrence of room temperature ferromagnetism is demonstrated in pulsed laser deposited thin films of Sn1-xCoxO2-d (x<0.3). Interestingly, films of Sn0.95Co0.05O2-d grown on R-plane sapphire not only exhibit ferromagnetism with a Curie…

Magnetometry, x-ray, and neutron scattering have been used to study the structural and magnetic properties of a TbMnO3 thin film grown on a [001] SrTiO3 substrate by pulsed laser deposition. Although bulk TbMnO3 is a low temperature…

Ferromagnetism was observed in a Pt(100) ultrathin film deposited on a SrTiO3(100) substrate. The ferromagnetism, which appears in films with thicknesses of 2.2-4.4 nm, periodically changes with a period of approximately 1 nm (5-6…

The copper ferrite thin films have been deposited by RF sputtering at a 50W rf power. The As-deposited films are annealed in air at $800^{\circ}$C and then slow cooled. The As-deposited (AD) as well as slow cooled (SC) films are studied…

Room-temperature ferromagnetism is observed in (110) oriented ZnO films containing 5 at % of Sc, Ti, V, Fe, Co or Ni, but not Cr, Mn or Cu ions. There are large moments, 1.9 and 0.5 muB/atom for Co- and Ti-substituted oxides, respectively.…

Ferromagnetic properties of In1-xMnxAs thin films were investigated. Room temperature ferromagnetic order was observed in nominally single-phase films with x = 0.01-0.10. Magnetization measurements indicated that these In1-xMnxAs samples…

The linear magnetoelectric effect was measured in 500 nm Cr2O3 films grown by rf sputtering on Al2O3 substrates between top and bottom thin film Pt electrodes. Magnetoelectric susceptibility was measured directly by applying an AC electric…

50nm thick nanogranular polycrystalline dysprosium thin films have been prepared via ultra-high vacuum DC sputtering on SiO2 and Si wafers. The maximum in-plane spontaneous magnetization at T = 4K was found to be MS4K = 3.28T for samples…

We provide evidence for a finite temperature ferromagnetic transition in 2-dimensions as $H \to 0$ in thin films of $^3$He on graphite, a model system for the study of two-dimensional magnetism. We perform pulsed and CW NMR experiments at…