Bulk MgB2 - based materials with the following critical current densities (jc) in 1 T field: 570 kA/cm^2 at 10 K, 350 kA/cm^2 at 20 K and 40 kA/cm^2 at 30 K and in 10 T field: 650 A/cm^2 at 10 K have been high-pressure (HP) synthesized from…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…
A new route to the sintering of MgB2 has been identified, based on a reactive infiltration of liquid Mg on a powdered B preform. The technique allows to obtain large bulk manufacts in an inexpensive way, without the need of high pressure…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Polycrystalline MgB2 samples with GaN additions were prepared by reaction of Mg, B, and GaN powders. The presence of Ga leads to a low melting eutectic phase which allowed liquid phase sintering and produces plate-like grains. For low-level…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
We have investigated the microstructure, normal-state electrical connectivity, and critical current density of ex-situ MgB2 polycrystalline bulks prepared by systematically varying the sintering conditions under low pressure. Samples heated…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different…
The Powder-In-Tube process has been employed to fabricate tape-like conductors with a strong metallic sheath and based on the newly discovered MgB2 superconducting phase. Long superconducting tapes have been prepared by packing reacted MgB2…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
Magnetic field of up to 12 T was applied during the sintering process of pure MgB2 and carbon nanotube (CNT) doped MgB2 wires. We have demonstrated that magnetic field processing results in grain refinement, homogeneity and significant…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…