相关论文: Crack tip kinematics reveal the cohesive zone stru…
In fracture mechanics, polyacrylamide hydrogels have been widely used as a model material for experiments, benefited from its optical transparency, fracture brittleness, and low Rayleigh wave velocity. To describe the brittle fracture in…
Highly-deformable materials, from synthetic hydrogels to biological tissues, are becoming increasingly important from both fundamental and practical perspectives. Their mechanical behaviors, in particular the dynamics of crack propagation…
We analyse high resolution slip rate data obtained during dynamic shear rupture experiments by Berman et al. (2020). We use an inverse method to extract the details of strength evolution within the cohesive zone. The overall behaviour is…
We investigate phase-field modeling of brittle fracture in a one-dimensional bar featuring a continuous variation of elastic and/or fracture properties along its axis. Our main goal is to quantitatively assess how the heterogeneity in…
Crack fronts deform due to heterogeneities, and inspecting these deformations can reveal local variations of material properties, and help predict out of plane damage. Current models neglect the influence of a finite dissipation…
In studies of the dynamic failure of brittle hydrogels, a bound has been placed on the process zone scale - the scale where material separation and ultimate failure occur. For the polyacrylamide hydrogel system under study, this bound is…
Crack growth is the basic mechanism leading to the failure of brittle materials. Engineering addresses this problem within the framework of continuum mechanics, which links deterministically the crack motion to the applied loading. Such an…
We present high resolution measurements of the displacement and strain fields near the tip of a dynamic (Mode I) crack. The experiments are performed on polyacrylamide gels, brittle elastomers whose fracture dynamics mirror those of typical…
Hydrogels have had a profound impact in the fields of tissue engineering, drug delivery, and materials science as a whole. Due to the network architecture of these materials, imbibement with water often results in uniform swelling and…
A continuum model of fracture that describes, in principle, the propagation and interaction of arbitrary distributions of cracks and voids with evolving topology without a fracture criterion is developed. It involves a 'law of motion' for…
We argue that nucleation of brittle cracks in initially flawless soft elastic solids is preceded by a nonlinear elastic instability, which cannot be captured without accounting for geometrical precise description of finite elastic…
We use numerical simulations and an athermal quasi-static shear protocol to investigate the yielding of a model colloidal gel. Under increasing deformation, the elastic regime is followed by a significant stiffening before yielding takes…
We study the crackling noise emerging during single crack propagation in a specimen under three-point bending conditions. Computer simulations are carried out in the framework of a discrete element model where the specimen is discretized in…
We formulate a nonlocal cohesive model for calculating the deformation state inside a cracking body. In this model a more complete set of physical properties including elastic and softening behavior are assigned to each point in the medium.…
When a crack interacts with material heterogeneities, its front distorts and adopts complex tortuous configurations that are reminiscent of the energy barriers encountered during crack propagation. As such, the study of crack front…
We have designed a new experimental setup able to investigate fracture of soft materials at small scales. At high crack velocity, where energy is mostly dissipated through viscoelastic processes, we observe an increasingly large high strain…
It is widely known that freezing breaks soft, wet materials. However, the mechanism underlying this damage is still not clear. To understand this process, we freeze model, brittle hydrogel samples, while observing the growth of ice-filled…
Experiments on quasistatic crack propagation in gelatin hydrogels reveal a new branching instability triggered by wetting the tip opening with a drop of aqueous solvent less viscous than the bulk one. We show that the emergence of unstable…
Brittle materials fail catastrophically. In consequence of their limited flaw-tolerance, failure occurs by localized fracture and is typically a dynamic process. Recently, experiments on epithelial cell monolayers have revealed that this…
We consider a linearly elastic body consisting of two equal symmetrically arranged layers (or half-planes) connected by a structured interface as a prospective crack path. The interface is comprised by periodic discrete system of bonds. In…