Irradiation with 2.5 MeV electrons at doses up to 5.2 $\times$10$^{19}$ electrons/cm$^2$ was used to introduce point-like defects in single crystals of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ with $x=$ 0.19 ($T_c=$ 14 K), $x=$ 0.26 ($T_c=$ 32 K) and…
London penetration depth, $\lambda(T)$, was measured in single crystals of SrFe$_2$(As$_{1-x}$P$_x$)$_2$ ($x=$0.35) iron - based superconductor. The influence of disorder on the transition temperature, $T_c$, and on $\lambda(T)$ was…
In-plane surface Ka-band microwave impedance of optimally doped single crystals of the Fe-based superconductor Ba(Fe0.926Co0.074)2As2 (Tc= 22.8K) was measured. Sensitive sapphire disk quasi-optical resonator with high-Tc cuprate conducting…
Precision measurements of active and reactive components of in-plane microwave surface impedance were performed in single crystals of optimally-doped Fe-based superconductor Ba(Fe1-xCox)2As2 (x = 0.074, Tc = 22.8 K). Measurements in a…
Irradiation with Pb ions was used to study the effect of disorder on the in-plane London penetration depth, $\lambda(T)$, in single crystals of Ba(Fe$_{1-x}$T$_x$)$_2$As$_2$ (T=Co, Ni). An increase of the irradiation dose results in a…
A single crystal of isovalently substituted Ba(Fe$_{1-x}$Ru$_{x}$)$_2$As$_2$ ($x=0.24$) was sequentially irradiated with 2.5 MeV electrons up to a maximum dose of $2.1 \times 10^{19}$ electrons/cm^2. The electrical resistivity was measured…
Temperature dependence of the London penetration depth $\lambda$ measured in single crystals of CeCoIn$_5$ is interpreted as caused by a strong pair-breaking scattering that makes the superconductivity in this compound gapless. For a…
The London penetration depth, $\lambda(T)$, has been measured in several single crystals of Ba(Fe$_{0.93}$Co$_{0.07}$)$_2$As$_2$. Thermodynamic, electromagnetic, and structural characterization measurements confirm that these crystals are…
The in-plane London penetration depth, $\lambda(T)$, was measured in single crystals of the iron-chalcogenide superconductors Fe$_{1.03}$(Te$_{0.63}$Se$_{0.37}$) and Fe$_{1.06}$(Te$_{0.88}$S$_{0.14}$) by using a radio-frequency tunnel diode…
Unconventional superconductivity has long been believed to arise from a lab-grown correlated electronic system. Here we report compelling evidence of unconventional nodal superconductivity in a mineral superconductor \rhs. We investigated…
London penetration depth, $\lambda (T)$, was measured in single crystals of K$_{1-x}$Na$_x$Fe$_2$As$_2$, $x$=0 and 0.07, down to temperatures of 50~mK, $\sim T_c/50$. Isovalent substitution of Na for K significantly increases impurity…
The London penetration depth was measured in optimally doped Ba0.6K0.4Fe2As2 crystals, with and without columnar defects produced by 1.4 GeV 208Pb irradiation. The low temperature behavior of unirradiated samples was consistent with a fully…
The London penetration depth is evaluated for isotropic materials for any transport and pair-breaking Born scattering rates. Besides known results, a number of new features are found. The slope $|d\rho/d\theta |$ of the normalized…
The investigation of the penetration depth \lambda_{ab}(T,p) in YBa_2Cu_3O_{7-x} crystals allowed to observe the following features of the superfluid density n_s(T,p)\propto \lambda_{ab}^{-2}(T,p) as a function of temperature T<Tc/2 and…
Irradiation with 1.4 GeV $^{208}$Pb ions was used to induce artificial disorder in single crystals of iron-arsenide superconductor Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ and to study its effect on the temperature-dependent London penetration depth…
The London penetration depth, $\lambda(T)$, was measured in a single crystal V$_{3}$Si. The superfluid density obtained from this measurement shows a distinct signature of two almost decoupled superconducting gaps. This alone is…
The temperature dependence of the London penetration depth,lambda(T), was measured in both single crystal and polycrystalline MgB_2 samples by a high-resolution, radio frequency technique. A clear exponential temperature dependence of…
The temperature dependence of the in-plane, \lambda_{\parallel}, and interplane, \lambda_{\perp}, London penetration depth was measured in the metal-free all-organic superconductor \beta-ET (see title) ($T_c \approx$ 5.2 K).…
The temperature dependence of the London penetration depth, $\lambda(T)$, was measured in polycrystalline MgB$_2$ samples by a high-resolution, radio frequency technique. A clear exponential temperature dependence of $\lambda(T)$ was…
We have characterized an electron-irradiated Ba1-xKxFe2As2 (x = 0.53) single-crystal using two different experimental techniques: magneto-optic measurements and microwave measurements. The crystal has been measured before as well as after…