相关论文: Fabrication of highly dense isotropic Nd-Fe-B bond…

Magnetic isotropic NdFeB powder is processed by the following additive manufacturing methods: (i) stereolithography (SLA), (ii) fused filament fabrication (FFF), and (iii) selective laser sintering (SLS). For the first time, a…

The possibility of producing polymer-bonded magnets with the aid of additive processes, such as 3D printing, opens up a multitude of new areas of application. Almost any structures and prototypes can be produced cost-effectively in small…

3D print is a recently developed technique, for single-unit production, and for structures that have been impossible to build previously. The current work presents a method to 3D print polymer bonded isotropic hard magnets with a low-cost,…

For two decades, NdFeB based magnets have been a critical component in a range of electrical devices engaged in energy production and conversion. The magnet shape and the internal microstructure of the selected NdFeB grade govern their…

Nd-Fe-B bonded magnets are an important class of permanent magnets, employed in many technological sectors. The Additive Manufacturing (AM) processes enables the fabrication of net-shape bonded magnets with complex geometries, allowing to…

5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…

Additive manufacturing of polymer bonded magnets is a recently developed technique, for single-unit production, and for structures that have been impossible to manufacture previously. Also new possibilities to create a specific stray field…

Here, we report wafer scale fabrication of densely packed Fe nanostripe-based magnetic thin films on a flexible substrate and their magnetic anisotropy properties. We find that Fe nanostripes exhibit large in-plane uniaxial anisotropy and…

Ta (100 nm) / NdFeB (5 $\mu$m) / Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ~ 18 $\mu$m/h). A 2-step procedure was used : deposition at temperatures up to 400 C followed by ex-situ…

Two-dimensional (2D) materials showing room-temperature magnetism and high coercivity are desired for combining magnetism with semiconducting properties useful for spintronics. In this work, the magnetic properties of the 1T phase of…

The magnetization (M) as a function of temperature (T) from 2 to 300 K and in-plane field (H) up to 1 kOe, room temperature easy and hard direction in-plane field hysteresis loops for fields between -100 and +100 Oe, and 10 GHz…

The electrical machinery core is formed with a ferromagnetic material that offers high magnetic properties. As ferromagnetic materials have high relative magnetic permeability, they are important in the formation of electromagnetic device…

Due to the resource criticality of rare-earths (RE), an alternative to the well-known Nd$_2$Fe$_{14}$B magnets with a lower amount of critical elements is required. In this work, density functional theory (DFT) calculations to investigate…

In this publication we describe the extrusion process and the properties of polymer-bonded anisotropic SrFe$_\text{12}$O$_\text{19}$ filaments for fused filament fabrication (FFF). Highly filled polyamide 12 filaments with a filling…

Nb and its compounds are widely used in quantum computing due to their high superconducting transition temperatures and high critical fields. Devices that combine superconducting performance and spintronic non-volatility could deliver…

We have measured the magnetoresistance of stretched sheets of carbon nanotubes in temperatures ranging from 2 K to 300 K and in magnetic fields up to 9 T, oriented either perpendicular or parallel to the plane of the sheets. The samples…

Bulk metallic samples were synthesized from different binary powder mixtures consisting of elemental Cu, Co, and Fe using severe plastic deformation. Small particles of the ferromagnetic phase originate in the conductive Cu phase, either by…

We present the fabrication of metallic magnetic nanowires using a low temperature chemical process. We show that pressed powders and magnetically oriented samples exhibit a very high coercivity (6.5 kOe at 140 K and 4.8 kOe at 300 K). We…

Ni-Mn-based Heusler alloys like Ni-Mn-Sn show an elastocaloric as well as magnetocaloric effect during the magneto-structural phase transition, making this material interesting for solid-state cooling application. Material processing by…

High-pressure torsion (HPT), a technique of severe plastic deformation (SPD), is shown as a promising processing method for exchange-spring magnetic materials in bulk form. Powder mixtures of Fe and SmCo$_{5}$ are consolidated and deformed…