相关论文: Enhanced critical-current in P-doped BaFe2As2 thin…

The most effective way to enhance the dissipation-free supercurrent in presence of magnetic field for type II superconductors is the introduction of defects that acts as artificial pinning centres (APCs) for the vortices. For instance, the…

High critical current densities (Jc) > 1 MA/cm2 were realized in cobalt-doped BaFe2As2 (BaFe2As2:Co) films on flexible metal substrates with biaxially-textured MgO base-layers fabricated by an ion-beam assisted deposition technique. The…

High temperature (high-Tc) superconductors like cuprates have superior critical current properties in magnetic fields over other superconductors. However, superconducting wires for high-field-magnet applications are still dominated by…

The K- and Co-doped BaFe2As2 (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (Hc2) of well over 50 T, Hc2 anisotropy Gamma < 2, and thin film critical current densities…

Microstructura lly clean, isov alently P-doped BaFe2As2 (Ba-122) single crystalline thin films have been prepared on MgO (001) substrates by molecular beam epitaxy. These films show a superconducting transition temperature (Tc) of over 30 K…

We optimized the substrate temperature (Ts) and phosphorus concentration (x) of BaFe2(As1-xPx)2 films on practical metal-tape substrates for pulsed laser deposition from the viewpoints of crystallinity, superconductor critical temperature…

High critical current densities Jc of 4 MA/cm2 at 4 K were obtained in Co-doped BaFe2As2 (BaFe2As2:Co) epitaxial films grown directly on (La, Sr)(Al, Ta)O3 substrates by pulsed laser deposition. Use of a highly pure target and improvement…

Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly…

The biaxially textured growth of superconducting Co-doped BaFe2As2 (Ba-122) thin films has been realized on ion beam assisted deposition (IBAD) MgO coated conductor templates by employing an iron buffer architecture. The iron pnictide…

We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…

Superconducting joints are one of the key technologies to make Ba1-xKxFe2As2 (Ba-122) superconducting wires or tapes for high-field applications. Herein, superconducting joints were fabricated by a simple cold-pressing method, and the joint…

High critical temperature superconductors have zero power consumption and could be used to produce ideal electric power lines. The principal obstacle in fabricating superconducting wires and tapes is grain boundaries-the misalignment of…

We show that despite the low anisotropy, strong vortex pinning and high irreversibility field Hirr close to the upper critical field Hc2 of Ba(Fe1-xCox)2As2, the critical current density Jgb across [001] tilt grain boundaries (GBs) of thin…

Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…

We report herein a high and isotropic critical-current density Jc for BaFe2(As,P)2 epitaxial films. The isotropy of Jc with respect to the magnetic-field direction was improved significantly by decreasing the film growth rate to 2.2…

The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…

We demonstrate the growth of Co-doped BaFe2As2 (Ba-122) thin films on AEF2 (001) (AE: Ca, Sr, Ba) single crystal substrates using pulsed laser deposition. All films are grown epitaxially despite of a large misfit of -10.6% for BaF2…

Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…

We report the growth of potassium-doped BaFe2As2 thin films, where the major charge carriers are holes, on Al2O3 (0001) and LaAlO3 (001) substrates by using an ex-situ pulsed laser deposition technique. The measured Tc's are 40 and 39 K for…

Ba(Fe1-xCox)2As2 superconducting thin films have been grown on SrTiO3, (La,Sr)(Al,Ta)O3, LaAlO3 and YAlO3 (YAO) single crystal substrates by pulsed laser deposition. All the films, except on YAO, have been grown epitaxially without buffer…