相关论文: AC losses in high pressure synthesized MgB2 bulk r…
AC losses of granular superconducting MgB2 were measured using non-resonant rf power absorption techniques. The presence of two band-gaps makes the temperature dependent ac loss pattern of MgB2 different from other high Tc superconductors…
The DC magnetization and AC complex magnetic susceptibilities were measured for MgB2 single crystals, unsubstituted and carbon substituted with the composition of Mg(B_0.94C_0.06)2. The measurements were performed in AC and DC magnetic…
Studies on the new MgB2 superconductor, with a critical temperature Tc ~ 39 K, have evidenced its potential for applications although intense magnetic relaxation effects limit the critical current density, Jc, at high magnetic fields. This…
Based on DC magnetization measurements, the temperature dependencies of the trapped magnetic field have been calculated for two MgB2 samples prepared by two different techniques: the high-pressure sintering and the hot pressing.…
Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Cables made of MgB2 superconductors are currently explored as a viable solution for transporting high electrical power in the AC regime. In order to be competitive against the DC solution, the cables need to have an acceptable level of AC…
Bulk MgB2 samples were prepared under different synthesis conditions and analyzed by scanning and transmission electron microscopy. The critical current densities were determined from the magnetization versus magnetic field curves of bulk…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…
In the present investigation, we report a systematic study of Ag admixing in MgB2 prepared by solid-state reaction at ambient pressure. All the samples in the present investigation have been subjected to structural/ microstructural…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
If the critical current density Jc is very high for a superconductor, then estimating its value from transport measurements is not very easy. In such cases, the value of Jc, called Jcm for magnetic Jc, is usually obtained from the measured…
The current distribution and the AC loss in a composite superconducting tape containing a layer from magnetic material is calculated and compared with experiments, showing a very good agreement. The situations of an alternating uniform…
The AC loss in ReBCO coated conductors is large in situations when the conductors are subjected to a considerable magnetic field, like in rotating machines, transformers and high-field magnets. Roebel cables can reduce the AC loss in these…