Reflective cracking is a relatively premature distress that occurs in HMA materials overlaying cracked and jointed underlying pavements. The high concentration of stresses and strains in the vicinity of the discontinuity of the old pavement…
This study examines the effectiveness of HMA overlay design strategies for the purpose of controlling the development of reflective cracking. A parametric study was conducted using a 3D Finite Element (FE) model of a rigid pavement section…
Resurfacing a moderately deteriorated Portland cement concrete (PCC) pavement with asphalt concrete (AC) layers is considered an efficient rehabilitation practice. However, reflective cracks may develop shortly after resurfacing because of…
Increasing the HMA base thickness and modifying the HMA mixture properties to improve the resistance to fatigue cracking are among the most popular methods for achieving long-lasting pavements. Such methods are based on the idea of reducing…
Hyper-viscoelastic polymers have multiple areas of application including aerospace, biomedicine, and automotive. Their mechanical responses are therefore extremely important to understand, particularly because they exhibit strong rate and…
Thermal cracking in urban underground sidewalls is frequently observed when structures are cast in summer and enter service in winter, as seasonal temperature gradients act under structural restraint. To quantify the local stress field…
Synthetic waxes produced by standard and registered processes may be used to manufacture Warm Mix Asphalt (WMA), which is a modified asphalt concrete produced, applied and compacted at temperatures below those typically required. This…
The thermally activated motion of dislocations across fields of obstacles distributed at random and in a correlated manner, in separate models, is studied by means of computer simulations. The strain rate sensitivity and strength are…
We investigate the buckling and post-buckling properties of a hyperelastic half-space coated by two hyperelastic layers when the composite structure is subjected to a uniaxial compression. In the case of a half-space coated with a {\it…
The damage mechanisms and load redistribution of high strength TC17 titanium alloy/unidirectional SiC fibre composite (fibre diameter = 100 $\mu$m) under high temperature (350 {\deg}C) fatigue cycling have been investigated in situ using…
Sloped terrains tend to creep downward over time, even when their slope is below the nominal angle of repose. This behavior can result from periodic variations in environmental conditions, such as daily or seasonal fluctuations in…
Strain rate sensitivity is a key feature of material deformation, whose importance is growing both because miniaturized components experience higher effective rates and because small scale simulations increasingly probe such conditions. As…
A simple and robust spring-block model obeying threshold dynamics is introduced to study surface fracture of an overlayer subject to stress induced by adhesion to a substrate. We find a novel phase transition in the crack morphology and…
The mechanical performance of reinforced composites is strongly influenced at different scales by the stress transferred at the matrix-fibre interfaces and at any surface where material discontinuity occurs. In particular, the mechanical…
The existence of a very special ratcheting regime has recently been reported in a granular packing subjected to cyclic loading \cite{alonso04}. In this state, the system accumulates a small permanent deformation after each cycle. After a…
Cracking is a common failure mode in asphalt concrete (AC) pavements. Many tests have been developed to characterize the fracture behavior of AC. Accurate crack detection during testing is crucial to describe AC fracture behavior. This…
Refractory masonry (refractories) is exposed to in-service loads of different types. To rationalise the masonry design and failure analysis, differences of failure under cyclic and monotonic loading were studied. For samples of silica…
We experimentally characterize the impact response of concentrated suspensions of cornstarch and water. We hypothesize that the dynamically jammed region that propagates ahead of the impactor is responsible for the strong stress response to…
The water impact of an inclined flat plate and at high horizontal velocity is experimentally investigated with focus on the fluid-structure interaction aspects. Several test conditions have been examined by varying the vertical to…
As shown by strains measured on full scale experimental aircraft structures, traffic of slow-moving multiple loads leads to asymmetric transverse strains that can be higher than longitudinal strains at the bottom of asphalt pavement layers.…