The temperature and angle dependent resistivity of Ba(Fe$_{0.75}$Ru$_{0.25}$)$_2$As$_2$ single crystals were measured in magnetic fields up to 14 T. The temperature dependent resistivity with the magnetic field aligned parallel to c-axis…
We synthesized the new Fe-based superconductor K0.8Fe2Se2 single crystals. The obtained single crystal exhibited a sharp superconducting transition, and the onset and zero-resistivity temperature was estimated to be 33 and 31.8 K,…
The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…
Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…
We report the crystal growth and structural, magnetic, conductivity, and specific heat investigations of Rb(1-x)Fe(2-y)Se2 single crystals with varying stoichiometry prepared by self-flux and Bridgman methods. The system exhibits a strongly…
We successfully grew the high-quality single crystal of Rb$_{0.78}$Fe$_2$Se$_{1.78}$, which shows sharp superconducting transition in magnetic susceptibility and electrical resistivity. Resistivity measurements show the onset…
The transport and superconducting properties of Ba_{1-x}K_xFe_2As_2 single crystals with T_c = 31 K were studied. Both in-plane and out-of plane resistivity was measured by modified Montgomery method. The in-plane resistivity for all…
Single crystals of Tl0.58Rb0.42Fe1.72Se2 are successfully grown with the superconducting transition temperatures Tconset=32K and Tczero=31.4K. The Hall coefficient exhibits a multi-band behavior, which is very similar to that of all other…
The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature…
Sizable single crystals of $BaFe_2As_2$ have been grown with self-flux method. The crystals are plate-like with c-axis perpendicular to the plane. The size can be as large as 3 x 5 x 0.2 $mm^3$. The resistivity anisotropy…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
We have determined the resistive upper critical field Hc2 for single crystals of the superconductor Fe1.11Te0.6Se0.4 using pulsed magnetic fields of up to 60T. A rather high zero-temperature upper critical field of mu0Hc2(0) approx 47T is…
The anisotropic superconducting properties of single crystals of Cu0.07TiSe2 were studied by measurements of magnetization and electrical resistivity. TC is around 3.9 K, and the measured upper critical field (Hc2) values are ~1.25 T and…
Early work on the iron-arsenide compounds supported the view, that a reduced dimensionality might be a necessary prerequisite for high-Tc superconductivity. Later, however, it was found that the zero-temperature upper critical magnetic…
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated…
We have successfully grown high quality single crystals of SrFe$_2$As$_2$ and A$_{0.6}$K$_{0.4}$Fe$_2$As$_2$(A=Sr, Ba) using flux method. The resistivity, specific heat and Hall coefficient have been measured. For parent compound…
We report a study of anisotropy in transport and magnetic properties of K0.64Fe1.44Se2.00 single crystals. The anisotropy in resistivity is up to one order of magnitude between 1.8 K and 300 K. Magnetic susceptibility exhibits weak…
We have investigated temperature and angular dependence of resistivity of K0.70(7)Fe1.55(7)Se1.01(2)S0.99(2) and K0.76(5)Fe1.61(5)Se0.96(4)S1.04(5) single crystals. The upper critical fields Hc2(T) for both field directions decrease with…
We report resistivity measurements performed on KFe$_2$As$_2$ single crystals down to $T$ = 0.3 K and in magnetic fields up to 17.5 T. The in-plane resistivity vs. $T$ curve has a convex shape down to $\sim$50 K and shows a $T^2$ dependence…