A set of thin film Mn$_x$Si$_{1-x}$ alloy samples with different manganese concentration x = 0.44 - 0.63 grown by the pulsed laser deposition (PLD) method onto the Al$_2$O$_3$(0001) substrate was investigated in the temperature range 4 -…
The magnetoresistance (MR) of 10 nm to 200 nm thin polycrystalline Co-films, deposited on glass and insulating Si(100), is studied in fields up to 120 kOe, aligned along the three principal directions with respect to the current:…
We report the observation of ferromagnetic resonance (FMR) and the determination of the magnetocrystalline anisotropy in (100)-oriented single-crystalline thin film samples of GaMnP with x=0.042. The contributions to the magnetic anisotropy…
The suitability of a particular material for use in magnetic devices is determined by the process of magnetization reversal/relaxation, which in turn depends on the magnetic anisotropy. Therefore, designing new ways to control magnetic…
Magnetic anisotropy in complex oxides often originates from the complex interplay of several factors, including crystal structure, spin-orbit coupling, and electronic interactions. Recent studies on Ru-substituted $La_{0.70}Sr_{0.30}MnO_3$…
We have performed a systematic investigation of magnetotransport of a series of as-grown and annealed Ga1-xMnxAs samples with 0.011 <= x <= 0.09. We find that the anisotropic magnetoresistance (AMR) generally decreases with increasing…
We investigated the magnetic anisotropy ratio of thin sputtered polycrystalline MgB2 films on MgO substrates. Using high magnetic field measurements, we estimated an anisotropy ratio of 1.35 for T=0 K with an upper critical field of 31.74 T…
The microscopic magnetic properties of high-quality GdN thin films have been investigated by electron spin resonance (ESR) and ferromagnetic resonance (FMR) measurements. Detailed temperature dependence ESR measurements have shown the…
In this work we report the appearence of a large perpendicular magnetic anisotropy (PMA) in Fe$_{1-x}$Ga$_x$ thin films grown onto ZnSe/GaAs(100). This arising anisotropy is related to the tetragonal metastable phase in as-grown samples…
NdFeAs(O,F) thin films having different fluorine contents were grown on 5 deg. or 10 deg. vicinal cut MgO and CaF2 single crystalline substrates by molecular beam epitaxy. Structural characterisations by reflection high-energy electron…
SSMO5347 thin films (thicknesses ~200 nm) were deposited by on-axis dc magnetron sputtering on the single crystal LSAT (001) substrates. These films are oriented along the out of plane c-direction. The ferromagnetic and insulator-metal…
The temperature dependence of magnetic anisotropy in (113)A (Ga,Mn)As layers grown by molecular beam epitaxy is studied by means of superconducting quantum interference device (SQUID) magnetometry as well as by ferromagnetic resonance (FMR)…
The magnetoresistance in a series of Ga1-xMnxAs samples with 0.2 =< x =< 0.8 have been measured for three mutually orthogonal orientations of the external magnetic field. The anisotropy magnetoresistance decreases with increasing of the Mn…
We report the magnetic properties of yttrium iron garnet (YIG) thin films grown by pulsed laser deposition technique. The films were deposited on Si (100) substrates in the range of 15-50 nm thickness. Magnetic characterizations were…
We investigate magnetoresistance phenomena associated with the magnetization hard-axis collapse in polycrystalline Co thin films. Transport measurements reveal that, for specific orientations of the applied magnetic field, the system…
A model is studied for the theoretical description of nanoscale magnetic films with high perpendicular anisotropy. In the model the magnetic film is described in terms of single domain magnetic grains with Ising-like behavior, interacting…
Amorphous thin films of Tb$_{17}$Co$_{83}$ (a-Tb-Co) grown by magnetron co-sputtering exhibit changes in magnetic anisotropy with varying growth and annealing temperatures. The magnetic anisotropy constant increases with increasing growth…
The magnetic properties of (Ga,Mn)As thin films depend on both the Mn doping level and the carrier concentration. Using a post growth hydrogenation process we show that it is possible to decrease the hole density from 1.1021 cm-3 to <1017…
Perpendicular magnetization is essential for high-density memory application using magnetic materials. High-spin polarization of conduction electrons is also required for realizing large electric signals from spin-dependent transport…
The anisotropy of MgB2 is still under debate: its value, strongly dependent on the sample and on the measuring method, ranges between 1.2 and 13. In this work we present our results on a MgB2 c-oriented superconducting thin film. To…