The effects of Mg deficiency in MgB2 films grown by using hybrid physical-chemical vapor deposition were investigated after vacuum annealing at various temperatures. High-quality MgB2 films grown on c-cut Al2O3 substrates with different…
Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure.…
Growth of carbon substituted magnesium diboride Mg(B1-xCx)2 single crystals with 0<x<0.15 is reported and the structural, transport, and magnetization data are presented. The superconducting transition temperature decreases monotonically…
Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms.…
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
The effect of Li substitution for Mg and of Li-C co-substitution on the superconducting properties and crystal structure of MgB2 single crystals has been investigated. It has been found that hole doping with Li decreases the superconducting…
We discuss the important aspects of synthesis and crystal growth of MgB2 under high pressure (P) and temperature (T) in Mg-B-N system, including the optimisation of P-T conditions for reproducible crystal growth, the role of liquid phases…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
An extended study of the superconducting and normal-state properties of various as-grown and post-annealed RbxFe2-ySe2 single crystals is presented. Magnetization experiments evidence that annealing of RbxFe2-ySe2 at 413 K, well below the…
Clarifying the impact of Fe doping on the structural and superconducting properties of MgB2 is crucial, considering that iron is commonly used as a sheath material for the fabrication of metal-clad MgB2 wires and tapes. To date the effects…
The effect of annealing on the superconducting properties of niobium single crystals cut from the same master boule was studied by local and global magnetic measurements, as well as scanning tunneling microscopy (STM). The formation of…
Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39…
Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and…
In this paper, we reported the structural properties and superconductivity of Mg(B1-xCx)2 compounds. Powder x-ray diffraction results indicate that the samples crystallize in a hexagonal AlB2-type structure. Due to the chemical activity of…
The two-gap structure in the superconducting state of MgB_2 gives rise to unusual thermodynamic properties which depart markedly from the isotropic single-band BCS model, both in their temperature- and field dependence. We report and…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
Superconducting transition temperatures ($T_c$'s) of MgB$_2$, Mg$_{1-x}$Ca$_x$B$_2$, Mg$_{1-x}$Na$_x$B$_2$, and Mg$_{1-x}$Al$_x$B$_2$ are studied within the McMillan approximation using electronic and structural information obtained from…