相关论文: Inhomogeneity of Magnesium Diboride Structure and …
The study of high pressure (2 GPa) synthesized MgB2-based materials allows us to conclude that higher borides (with near MgB12 stoichiometry) and oxygen-enriched Mg-B-O inclusions can be pinning centers in nanostructural magnesium diboride…
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides…
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical…
High energy milling of MgB2 pre-reacted powder renders the material largely amorphous through extreme mechanical deformation and is suitable for mechanically alloying MgB2 with dopants including carbon. Bulk samples of milled C and MgB2…
Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full…
The enhancement of the critical current density (Jc(H)) of carbon and nano-SiC doped MgB2 is presented and compared. The upper critical field (Hc2) being determined from resistivity under magnetic field experiments is though improved for…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
Bulk MgB2 samples were prepared under different synthesis conditions and analyzed by scanning and transmission electron microscopy. The critical current densities were determined from the magnetization versus magnetic field curves of bulk…
We have fabricated a series of ex situ copper sheathed powder-in-tube MgB2 wires with 20% by volume Ag, Pb, In, and Ga metal added to the MgB2 powder. We find the transport critical current of these wires increases significantly with the…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
In this paper, we reported the structural properties and superconductivity of Mg(B1-xCx)2 compounds. Powder x-ray diffraction results indicate that the samples crystallize in a hexagonal AlB2-type structure. Due to the chemical activity of…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
We report variation of lattice structure in diborides (AB2) with different A atoms to identify the special case of MgB2 showing high Tc superconductivity. High purity MgB2 (Tc~39 K) has been prepared by direct reaction of the elements and…
The influence of the nature of the boron precursor on the superconducting properties of polycrystalline MgB2 was studied. Critical current densities for the MgB2 made from high purity amorphous boron are at least a factor of three higher…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Bulk MgB2 - based materials with the following critical current densities (jc) in 1 T field: 570 kA/cm^2 at 10 K, 350 kA/cm^2 at 20 K and 40 kA/cm^2 at 30 K and in 10 T field: 650 A/cm^2 at 10 K have been high-pressure (HP) synthesized from…
Oxygen was systematically incorporated in MBE grown MgB2 films using in-situ post-growth anneals in an oxygen environment. Connectivity analysis in combination with measurements of the critical temperature and resistivity indicate that…
We study the effect of nano(n)-SiC addition on the crystal structure, critical temperature (Tc), critical current density (Jc) and flux pinning in MgB2 superconductor. X-ray diffraction patterns show that all the samples have MgB2 as the…