相关论文: Superconductivity in layered iron Selenide induced…
Chemical doping has recently become a very important strategy to induce superconductivity especially in complex compounds. Distinguished examples include Ba-doped La$_2$CuO$_4$ (the first high temperature superconductor), K-doped BaBiO$_3$,…
The recent discovery of high temperature superconductivity in a layered iron arsenide has led to an intensive search to optimize the superconducting properties of iron-based superconductors by changing the chemical composition of the spacer…
We report the successful substitution of cobalt, nickel, and copper for iron in the 1038 phase parent compound Ca$_{10}$(FeAs)$_{10}$(Pt$_3$As$_8$) yielding Ca$_{10}$(Fe$_{1-x}$Co$_x$As)$_{10}$(Pt$_3$As$_8$),…
New iron selenide superconductors by intercalating smaller-sized alkali metals (Li, Na) and alkaline earths using high-temperature routes have been pursued ever since the discovery of superconductivity at about 30 K in KFe2Se2, but all have…
We report the superconductivity at above 30 K in a new FeSe-layer compound K0.8Fe2Se2 (nominal composition) achieved by metal K intercalating in between FeSe layers. It is isostructural to BaFe2As2 and possesses the highest Tc for…
By using solid state reaction method, we have synthesized the Pd-doped superconductor SrFe2-xPdxAs2. The systematic evolution of the lattice constants indicated that the Fe ions were successfully replaced by the Pd. By increasing the doping…
A new hight Tc Fe-based compound system, AFe2As2 with A = K, Cs, K/Sr and Cs/Sr has been found. Through electron-doping, Tc of the A = K and Cs compounds rises to ~37 K, and finally enter a spin-density-wave state (SDW) through further…
By substituting Fe with the 5d-transition metal Pt in BaFe2As2, we have successfully synthesized the superconductors BaFe2-xPtxAs2. The systematic evolution of the lattice constants indicates that the Fe ions were successfully replaced by…
Pure phases of a new oxyarsenide superconductor of the nominal composition CeOFe0.9Co0.1As was successfully synthesized by solid state reaction in sealed silica ampoules at 1180 C. It crystallizes in the layered tetragonal ZrCuSiAs type…
Iron Selenide, Fe1.01Se, the layered parent compound of the recently discovered superconducting arsenide family, has previously been shown to be non magnetic and superconducting with a critical temperature of 8 K. Here we show that copper…
The recent discovery of high-temperature superconductivity in single-layer iron selenide has generated significant experimental interest for optimizing the superconducting properties of iron-based superconductors through the lattice…
Iron selenide (FeSe) - the structurally simplest iron-based superconductor, has attracted tremendous interest in the past years. While the transition temperature (Tc) of bulk FeSe is $\sim$ 8 K, it can be significantly enhanced to 40 - 50 K…
The ternary iron arsenide BaFe2As2 becomes superconducting by hole doping, which was achieved by partial substitution of the barium site with potassium. We have discovered bulk superconductivity up to Tc = 38 K in (Ba1-xKx)Fe2As2 with x =…
We have successfully grown single crystalline NaFeAs with cobalt or phosphor doping. Bulk superconductivity occurs in NaFe$_{0.95}$Co$_{0.05}$As at 19 K while much higher transition temperature is observed in NaFeAs$_{0.8}$P$_{0.2}$, in…
Arsenic doping in silicides has been much less studied compared with phosphorus. In this study, superconductivity is successfully induced by As doping in Mo$_5$Si$_3$. The superconducting transition temperature ($T_c$) reaches 7.7 K, which…
Superconductivity with transition temperature Tc above 40 K was observed in protonated FeSe (Hy-FeSe) previously with the ionic liquid of EMIM-BF4 used in the electrochemical process. However, the real superconducting phase is not clear…
Electron-doping of the semimetal (CeOFeAs) by either fluorine (max Tc ~ 43 K)or cobalt (max Tc ~ 11 K) leads to superconductivity. Here we show the effect of transition metal (Co) substitution at the iron site on the superconducting…
In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…
A superconducting transition temperature Tc as high as 100 K was recently discovered in 1 monolayer (1ML) FeSe grown on SrTiO3 (STO). The discovery immediately ignited efforts to identify the mechanism for the dramatically enhanced Tc from…
A1-xFe2-ySe2 (A = K, Cs, Rb, Tl) are recently discovered iron-based superconductors with critical temperatures (Tc) ranging up to 32 K. Their parent phases have unique properties when compared with other iron-based superconductors; e.g.,…