相关论文: Mechanical properties of reinforced MgB2 wires
Monofilamentary MgB2-wires with a 2- or 3-component sheath containing mechanical reinforcing stainless steel (SS) were prepared and characterized. In direct contact to the superconductor Nb, Ta or Fe was used. For a selection of samples…
Monofilamentary MgB2-wires with a mechanical tough Nb/Cu/steel or Fe/steel sheath were prepared and characterized. The steel content was varied to investigate the reinforcement effect and the consequences for the superconducting properties…
In this contribution, different concepts for mechanically reinforced MgB2 wires with high transport currents are presented and characterised. It is shown that the achieved critical transport currents depend strongly on the conductor…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…
MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary…
The influence of mechanical strain on the critical current (Ic) is investigated for MgB2/stainless steel (SUS316) superconducting tapes. The tapes are fabricated by using 'powder in tube' method and deformation process without any heat…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
Seven years after the discovery of superconductivity in magnesium diboride, the fundamental superconducting properties of this compound are well known and the peculiar current transport in polycrystalline materials is essentially…
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…
The influence of two important features of magnesium diboride on the macroscopic transport properties of polycrystalline MgB2 is discussed in the framework of a percolation model. While two band superconductivity does not have significant…
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the…
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density…
The intrinsic properties of MgB$_2$ form the basis for all applications of this superconductor. We wish to emphasize that the application range of polycrystalline MgB$_2$ is limited by the upper critical field H$_{c2}$ and its anisotropy.…
Transport critical current (Ic) was measured for Fe-sheathed MgB2 round wires. A critical current density of 5.3 x 10^4 A/cm^2 was obtained at 32K. Strong magnetic shielding by the iron sheath was observed, resulting in a decrease in Ic by…
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2…
The Powder-In-Tube process has been employed to fabricate tape-like conductors with a strong metallic sheath and based on the newly discovered MgB2 superconducting phase. Long superconducting tapes have been prepared by packing reacted MgB2…
In DC and AC practical applications of MgB2 superconducting wires an important role is represented by the material sheath which has to provide, among other things, a suitable electrical and thermal stabilization. A way to obtain a large…