相关论文: Improvement of critical current in MgB2/Fe wires b…
Transport critical current (Ic) was measured for MgB2/Fe round wires, with magnetic field oriented perpendicular to the wire and parallel to it. Measurements were made on a wire with pure MgB2 core and another wire where MgB2 core was doped…
Magnesium diboride superconducting wires give the largest critical current density (Jc) when produced with iron sheath. Because iron is ferromagnetic, it is expected to improve the field dependence of Jc by shielding of the external field…
Local magneto-optical imaging and global magnetization measurement techniques were used in order to visualize shielding effects in the superconducting core of MgB_2 wires sheathed by ferromagnetic iron (Fe). The magnetic shielding can…
Monofilamentary MgB2-wires with a 2- or 3-component sheath containing mechanical reinforcing stainless steel (SS) were prepared and characterized. In direct contact to the superconductor Nb, Ta or Fe was used. For a selection of samples…
Magnetic measurements carried out on MgB_2 superconducting round wires have shown that the critical current density J_c(B_a) in wires sheathed by iron can be significantly higher than that in the same bare (unsheathed) wires over a wide…
Interaction between the superconductor and ferromagnet in MgB2/Fe wires results in either a plateau or a peak effect in the field dependence of transport critical current, Ic(H). This is in addition to magnetic shielding of external field.…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We have fabricated a series of ex situ copper sheathed powder-in-tube MgB2 wires with 20% by volume Ag, Pb, In, and Ga metal added to the MgB2 powder. We find the transport critical current of these wires increases significantly with the…
The nano-SiC doped MgB2/Fe wires were fabricated using a powder-in-tube method and an in-situ reaction process. The depression of Tc with increasing SiC doping level remained rather small due to the counterbalanced effect of Si and C…
We report significant transport critical currents firstly achieved in Sr0.6K0.4Fe2As2 wires and tapes with a Tc = 34 K, which were fabricated through an in-situ powder-in-tube process. Silver was used as a chemical addition as well as a…
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter…
We fabricated (Ba,Na)Fe2As2 superconducting wires using the powder-in-tube method and hot isostatic pressing. By improving powder synthesis processes compared with previous studies, highly pure raw materials for the wire fabrication were…
We demonstrate a large enhancement of critical current density (Jc) up to 1.0x10^7 A/cm2 at 5 K under self-field in (Ba,K)Fe2As2 single crystals by irradiating 320 MeV Au ions. With the very promising potential of this material in mind, we…
Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…
Recent advances in MgB2 conductors are leading to a new level of performance. Based on the use of proper powders, proper chemistry, and an architecture which incorporates internal Mg diffusion (IMD), a dense MgB2 structure with not only a…
The powder in tube method has been used to fabricate Ag and Cu clad MgB2 wires using an in-situ reaction method. The effects of short time sintering on the critical current densities of Ag and Cu clad MgB2 wires were studied. All the…
(Ba,K)Fe2As2 superconducting wires and tapes are fabricated by using hot isostatic pressing (HIP) technique, and their superconducting properties are studied. In the HIP round wire, transport critical current density (Jc) at 4.2 K has…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…
Monofilamentary MgB2-wires with a mechanical tough Nb/Cu/steel or Fe/steel sheath were prepared and characterized. The steel content was varied to investigate the reinforcement effect and the consequences for the superconducting properties…