Magneto-opitcal studies of a c-oriented epitaxial MgB2 film with critical current density 10^7 A/cm^2 demonstrate a breakdown of the critical state at temperatures below 10 K [cond-mat/0104113]. Instead of conventional uniform and gradual…
Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…
An extended magneto-optical (MO) analysis of samples cut from high-density pellets of MgB2 is reported. For sake of comparison some magnetic measurements and critical values are also shown. Notwithstanding the fact that the optical and SEM…
The distribution of magnetic field in single-phase polycrystalline bulk MgB2 has been measured using a Magneto-Optical (MO) technique for an external magnetic field applied perpendicular to the sample surface. The MO studies indicate that…
Bulk MgB2 samples were prepared under different synthesis conditions and analyzed by scanning and transmission electron microscopy. The critical current densities were determined from the magnetization versus magnetic field curves of bulk…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
Polycrystalline MgB2 samples with GaN additions were prepared by reaction of Mg, B, and GaN powders. The presence of Ga leads to a low melting eutectic phase which allowed liquid phase sintering and produces plate-like grains. For low-level…
We report phase formation, and detailed study of magnetization and resistivity under magnetic field of MgB2 polycrystalline bulk samples prepared by Fe-tube encapsulated and vacuum (10-5 torr) annealed (750 0C) route. Zero-field-cooled…
Magnetic relaxation and critical current density have been measured on a $MgB_2$ thin film in a wide region of temperature with the magnetic field up to 8 T. The irreversibility line has also been determined. It is found that the relaxation…
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
Magnetic instability in both ultra-pure and carbon-doped MgB2 films is investigated by magneto-optical imaging, transport and bulk magnetization measurements. In the carbon-doped MgB2 thin film, familiar dendritic flux-jump patterns were…
We study the magnetization of a cylindrical type-II superconductor filament covered by a coaxial soft-magnet sheath and exposed to an applied transverse magnetic field. Examining penetration of magnetic flux into the superconductor core of…
Magnetic flux distribution across a high-temperature superconductor strip is measured using magneto-optical imaging at 15 K. Both the current-carrying state and the remanent state after transport current are studied up to the currents 0.97…
The recent discovery of intermediate-temperature superconductivity (ITC) in MgB2 by Akimitsu et al. and its almost simultaneous explanation in terms of a hole-carrier-based pairing mechanism by Hirsch, has triggered an avalanche of studies…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
In the present investigation, we report a systematic study of Ag admixing in MgB2 prepared by solid-state reaction at ambient pressure. All the samples in the present investigation have been subjected to structural/ microstructural…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The critical-state in a thin strip of YBaCuO is studied by magneto-optical imaging. The distribution of magnetic flux density is shown to have a specific symmetry in the remanent state after a large applied field. The symmetry was predicted…