相关论文: Synthesis and Processing of $MgB_2$ powders and wi…
$MgB_2$ becomes superconducting just below 40 K. Whereas porous polycrystalline samples of $MgB_2$ can be synthesized from boron powders, in this letter we demonstrate that dense wires of $MgB_2$ can be prepared by exposing boron filaments…
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT…
We have fabricated a series of iron-sheathed superconducting wires prepared by the powder-in-tube technique from (MgB_2)_{1-x}:(Mg+2B)_x initial powder mixtures taken with different proportions, so that x varies from 0 to 1. It turned out…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different…
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
We succeeded in the fabrication of high-Jc MgB2/Fe wires applying the internal Mg diffusion (IMD) process with pure Mg core and SiC addition. A pure Mg rod with 2 mm diameter was placed at the center of a Fe tube, and the space between Mg…
In this paper we report a new synthesis route to produce boron powders characterized as being amorphous and having very fine particle size. This route has been developed to improve the performances of superconducting MgB2 powders, which can…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the…
We report the study of the polycrystalline MgB2 phase formation during the fabrication processes. Three major phases are identified in different sintering temperature ranges according to the corresponding superconducting properties and the…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB2 powders. It was found that linked superconducting structure is formed down to the minimum normalized density gamma= d/do= 0.16…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
A series of doping experiments are reported for MgB2 conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition(CVD) methods. Undoped MgB2 samples prepared from CVD prepared fibers consistently give…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…