The endpoint slippage analysis can be used to quantify the reduction and oxidation side-reactions occurring in rechargeable batteries. Application of this technique often disregards the interference of additional aging modes, such as…

It is shown that continuously occurring electrolyte-reduction reaction on freshly-exposed electrode surfaces during lithiation/delithiation cycles causes the lowering of cycling efficiency, and hence, capacity fade in well-cycled silicon…

A significant problem associated with batteries is the rapid reduction of charge-storage capacity with increasing charge/discharge rate. For example, improving this rate-performance is required for fast-charging of car batteries.…

Silicon-containing lithium-ion batteries can exhibit capacity gain early in life, which makes forecasting future cell behavior difficult. We have observed these anomalous trends even in conditions where known mechanisms, such as overhang…

An important objective of designing lithium-ion rechargeable battery cells is to maximize their rate performance without compromising the energy density, which is mainly achieved through computationally expensive numerical simulations at…

Cycle life is critically important in applications of rechargeable batteries, but lifetime prediction is mostly based on empirical trends, rather than mathematical models. In practical lithium-ion batteries, capacity fade occurs over…

Batteries are pivotal components in overcoming some of today's greatest technological challenges. Yet to date there is no self-consistent atomistic description of a complete battery. We take first steps toward modeling of a battery as a…

Non-aqueous metal-oxygen batteries depend critically on the reversible formation/decomposition of metal oxides on cycling. Irreversible parasitic reactions cause poor rechargeability, efficiency, and cycle life and have predominantly been…

With the importance of Li-ion and emerging alternative batteries to our electric future, predicting new sustainable materials, electrolytes and complete cells that safely provide high performance, long life, energy dense capability is…

Identifying overpotential components of electrochemical systems enables quantitative analysis of polarization contributions of kinetic processes under practical operating conditions. However, the inherently coupled kinetic processes lead to…

Battery interfaces help govern rate capability, safety/stability, cycle life, and self-discharge, but significant gaps remain in our understanding at atomic length scales that can be exploited to improve interfacial properties. In…

Capacity and coulombic efficiency are often used to assess the performance of Li-ion batteries, under the assumption that these quantities can provide direct insights about the rate of electron consumption due to growth of the solid…

In this study, we address the challenge of electrolyte degradation in all-solid-state humidified Li-$O_2$ batteries, which offer high theoretical energy density and potential cost advantages over conventional lithium-ion batteries.…

Lithium-ion batteries dominate battery research and industry due to their long research history and high energy density. However, increasing demand and limited lithium resources have raised lithium prices and battery costs, motivating…

Next-generation lithium-ion batteries with silicon anodes have positive characteristics due to higher energy densities compared to state-of-the-art graphite anodes. However, the large volume expansion of silicon anodes can cause high…

The prediction of battery rate performance traditionally relies on computation-intensive numerical simulations. While simplified analytical models have been developed to accelerate the calculation, they usually assume battery performance to…

Superoxide-based non-aqueous metal oxygen batteries have received considerable research attention, as they exhibit high energy densities and round-trip efficiencies. The cycling performance, however, is still poor. Here we study the cycling…

Electrolyte reduction products form the solid-electrolyte interphase (SEI) on negative electrodes of lithium-ion batteries. Even though this process practically stabilizes the electrode-electrolyte interface, it results in continued…

Renewable energy is critical for combating climate change, whose first step is the storage of electricity generated from renewable energy sources. Li-ion batteries are a popular kind of storage units. Their continuous usage through…

Battery aging is a natural process that contributes to capacity and power fade, resulting in a gradual performance degradation over time and usage. State of Charge (SOC) and State of Health (SOH) monitoring of an aging battery poses a…