Superconducting critical currents $j_{c} > 10^{5}$ A/cm$^{2}$ at temperatures $T \sim 50$ K and magnetic fields $B \sim 6$ T are reported for the YBa$_{2}$Cu$_{3-x}$Mo$_{x}$O$_{7+d}$ compound with $x = 0.02$. Clear evidence for the…
Detailed measurements of the critical current density jc of YBa2Cu3O7 films grown by pulsed laser deposition reveal the increase of jc as function of the filmthickness. Both this thickness dependence and the field dependence of the critical…
The dependence of the critical current density Jc on hydrostatic pressure to 0.6 GPa is determined for a single 25-degree [001]-tilt grain boundary in a bicrystalline ring of nearly optimally doped melt-textured YBa2Cu3Ox. Jc is found to…
The critical current (Jc) of highly twinned YBa2Cu3O7 films has been measured as a function of temperature, magnetic field and angle. For much of the parameter space we observe a strong suppression of Jc for fields in the twin boundary (TB)…
Mo-substituted triple perovskite superconducting samples with the stoichiometric composition La(1.5)Nd(0.5)Ca(1)Ba(2)[Cu(1-x)Mo(x)](5)O(z), [LNCBCuMO] with x = 0.00, 0.01, 0.03, 0.05 and 0.10, have been investigated using X-ray diffraction,…
We report on measurements on Y1-xPrxBa2Cu3O7-delta single crystals, with x varying from 0 to 2.4%. The upper and the lower critical fields, Hc2 and Hc1, the Ginzburg-Landau parameter and the critical current density, Jc(B), were determined…
The in-field critical current of commercial YBa2Cu3O7 coated conductors can be substantially enhanced by post-fabrication irradiation with 4 MeV protons. Irradiation to a fluence of 8x10^16 p/cm^2 induces a near doubling of the critical…
By using post-annealing and quenching technique, we show that the critical current density Jc,ab of KxFe2-ySe2 single crystals can be enhanced more than one order of magnitude up to ~ 2.1 \times 10^4 A/cm^2 at 1.8 K. The scaling law between…
We report DC isothermal magnetization, global critical current density (JC), Intra-grain critical current density (JCintra) and resistive upper critical field (Bc2) of polycrystalline Y1-xCaxBa2Cu3O7-{\delta} (YBCO); x = 0.00, 0.05, 0.10,…
Strong pinning depends on the pinning force strength and number density of effective defects. Using hydrostatic pressure method, we demonstrate that hydrostatic pressure up to 1.2 GPa can significantly enhance flux pinning or Jc by a factor…
We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by…
Temperature dependence of the zero-field critical current density, Jc0(T), in the CuO2 planes has been investigated for c-axis oriented YBa2Cu3O7-d (Y123) thin films with different hole content, p. p-values were varied by changing the…
Critical current density is the key parameter for the practical application of superconductivity. In this study, 3 MeV proton irradiation experiments were conducted on HgBa$_2$Ca$_2$Cu$_3$O$_8$$_+$$_\delta$ single crystals to introduce…
There are numerous potential applications for superconducting tapes, based on YBa2Cu3O7-x (YBCO) films coated onto metallic substrates. A long established goal of more than 15 years has been to understand the magnetic flux pinning…
The influence of adding 23 nm NiO nanoparticles on the magnetic hysteresis loops and critical current density of the high-temperature superconductor YBa2Cu3O7-d has been investigated. The samples were prepared using a fast annealing method…
Combined action of weak and strong pinning centers on the vortex lattice complicates magnetic behavior of a superconductor since temperature and magnetic field differently affect weak and strong pinning. In this paper we show that…
Polycrystalline La2-xPrxCa2xBa2Cu4+2xOz (LPCaBCO) compounds with x = 0.1 - 0.5 were synthesized by solid-state reaction method and studied by room temperature X-ray diffraction, dc resistivity, dc magnetization and iodometry. The…
We report the influence of 6 MeV Zr$^{4+}$ irradiation and post-irradiation annealing (200 {\deg}C) in the in-field dependences of the critical current densities J$_c$ of 1.3 $\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by…
The addition of artificial pinning centers has led to an impressive increase in critical current density ($J_{\rm c}$) in a superconductor, enabling record-breaking all-superconducting magnets and other applications. $J_{\rm c}$ has reached…
Large area arrays of through-thickness nanoscale pores have been milled into superconducting Nb thin films via a process utilizing anodized aluminum oxide thin film templates. These pores act as artificial flux pinning centers, increasing…