We investigate the microwave properties of epoxy-based composite containing melt-extracted CoFeBSiNb microwires fabricated by a combined current-modulation annealing (CCMA) technique. We observe a shift of the resonance peak in the…
Amorphous Co-rich microwires with excellent soft magnetic and mechanical properties produced by melt-extraction technique are emerging as a multifunctional material for a variety of applications ranging from ultrasensitive magnetic field…
A remarkably strong dependence of magnetoimpedance (MI) on tensile stress has been observed in the microwave frequency range for thin CoMnSiB glass-coated microwires exposed to a special thermal treatment. The MI ratio runs into more than…
The effect of tensile stress on magnetoimpedance (MI) in CoMnSiB amorphous wires at microwave frequencies (0.5-3 GHz) is investigated both experimentally and theoretically. In the presence of the dc bias magnetic field of the order of the…
High frequency [1-500 MHz] measurements of the magnetoimpedance (MI) of glass-coated Co$_{69.4}$Fe$_{3.7}$B$_{15.9}$Si$_{11}$ microwires are carried out with various metal-to-wire diameter ratios. A twin-peak, anhysteretic behaviour is…
Thin-film magnetic sensors using the giant magnetoimpedance (GMI) effect show great promise for sensitive low-field magnetic measurements. Optimising sensor performance requires a thorough understanding of the properties of various soft…
We have investigated for the first time the combined effect of current and stress on the GMI characteristics of vanishing-magnetostrictive Co-rich microwires at microwave frequency. As the current-annealed wire is subject to certain tensile…
High frequency [1-500 MHz] measurements of the Magneto-Impedance (MI) of glass-covered Co$_{69.4}$Fe$_{3.7}$B$_{15.9}$Si$_{11}$ microwires are carried out with various metal-to-wire diameter ratios. A twin-peak, anhysteretic behaviour is…
We have investigated the microwave properties of epoxy-based composites containing melt-extracted Co69.25Fe4. 25B13.5-xSi13Nbx (x=0, 1, 3) microwires of various length annealed using a so-called combined current-modulation annealing (CCMA)…
Magnetoimpedance, MI, change due to surface modification of the sensitive element caused by biofluids was studied with the aim of creating a robust sensor capable of separating the chemical surface modification from the sensing process. A…
A study of magnetic hysteresis and Giant magnetoimpedance (GMI) in amorphous glass covered Co-Si-B and Co-Mn-Si-B wires is presented. The wires, about 10 microns in diameter, were obtained by glass-coated melt spinning technique. Samples…
Motivated by the prospects of increased measurement bandwidth, improved signal to noise ratio and access to the full complex magnetic susceptibility we develop a technique to extract microwave voltages from our high resistance (10…
Composite wires with a three-layered structure exhibit a large giant magneto-impedance (GMI) effect, which can be used in sensitive magnetic field sensors. To further investigate the origin of the GMI effect, composite wires consisting of a…
Systematic measurements of stress-impedance (SI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at room temperature. The…
Systematic measurements of stress impedance (SI) and magneto-impedance (MI) have been carried out using Co-rich amorphous ribbons of nominal composition Co71-xFexCr7Si8B14 (x = 0, 2) at various excitation frequencies and bias fields and at…
The resistive and reactive components of magneto-impedance was studied for the as-quenched and microwave annealed amorphous Fe73.5Nb3Cu1Si13.5B9 ribbon as a function of biasing d.c magnetic fields (-60 to +60 Oe) and excitation frequencies…
This paper systematically studies the changes in the microstructure and magnetic properties of CoFeSiBNb$_3$ metallic microfibers before and after AC annealing. The influence of current intensity on the magneto-impedance (MI) effect of the…
We report a magnetic imaging method using atomic force microscopy to measure the locally induced anomalous Nernst effect. The tip contact creates a local temperature gradient on the sample surface controlled by a neighboring Joule heating…
The polycrystalline Mn1.26Fe0.60P0.48Si0.52 microwires were successfully fabricated for the first time by the melt-extraction technique, and their magnetic and magnetocaloric properties were investigated systematically. The structural…
We demonstrate composite media with ferromagnetic wires that exhibit a frequency region at the microwave regime with scattering spectra strongly dependent on an external magnetic field or stress. These tunable composite materials have…