A metallic surface is realized on stoichiometric and insulating (100) SrTiO$_3$ by Ar$^+$ - ion irradiation. The sheet carrier density and Hall mobility of the layer are $\sim$$4.0$ $\times$ $10^{14}$ $/cm^2$ and $\sim$$2$ $\times$ $10^3$…
The blue-green photoluminescence emitted by pure and electron-doped strontium titanate under intense pulsed near-ultraviolet excitation is studied experimentally, as a function of excitation intensity and temperature. Both emission spectra…
The resistivity of the two dimensional electron gas that forms at the interface of strontium titanate with various oxides is sensitive to irradiation with visible light. In this letter we present data on the interface between the band gap…
Following the recent surge of interest in n-doped strontium titanate as a possible blue light emitter, a time-resolved photoluminescence analysis was performed on nominally pure, Nb-doped and oxygen-deficient single-crystal SrTiO3 samples.…
Raman and Photoluminescence (PL) experiments on correlated metallic La$_{0.7}$Sr$_{0.3}$MnO$_{3}$ have been carried out using different excitation wavelengths as a function of temperature from 15 K to 300 K. Our data suggest a Raman mode…
It has been recently revealed that strontium titanate (SrTiO$_3$) displays persistent photoconductivity with unique characteristics: it occurs at room temperature and lasts over a very long period of time. Illumination of SrTiO$_3$ crystals…
In this work, we perform steady-state continuous wave (cw) photoluminescence (PL) measurements on a MAPbI$_3$ thin film in the temperature range of 10-160 K, using excitation densities spanning over almost seven orders of magnitude, in…
Samples of amorphous MgSiO_3 annealed at temperature steps leading up to their crystallisation temperature show a rise in photoluminescence activity, peaking at ~450C. The photoluminescence band has a main peak at 595nm and a weaker peak at…
Ferroelectric photovoltaic materials are an alternative to semiconductor-based photovoltaics and offer the advantage of above bandgap photovoltage generation. However, there are few known compounds, and photovoltaic efficiencies remain low.…
We investigated the ferroelectric properties of strontium titanate (STO) thin films deposited on SrTiO3 (001) substrate with SrRuO3 electrodes. The STO layer was grown coherently on the SrTiO3 substrate without in-plane lattice relaxation,…
We report a significant enhancement of room-temperature photoluminescence from trivalent erbium-doped (Er3+) silicon nitride (Si3N4) metasurfaces at the telecommunication wavelength prepared via ion implantation. The metasurfaces,…
Strain is an effective strategy to modulate the optoelectronic properties of 2D materials, but it has been almost unexplored in layered hybrid organic-inorganic metal halide perovskites (HOIPs) due to their complex band structure and…
Er-doped aluminum nitride films, containing different Er concentrations, were obtained at room temperature by reactive radio frequency magnetron sputtering. The prepared samples show a nano-columnar microstructure and the size of the…
We have studied the temperature dependencies of the photoluminescence (PL) intensity of 4.1 eV in microcrystalline powder of hexagonal boron nitride in the range of 7-1100 K. The results obtained have been analyzed within the band model of…
We investigate the cubic to tetragonal phase transition in the pressure-temperature phase diagram of strontium titanate SrTiO3 (STO) by means of Raman spectroscopy and X-ray diffraction on single crystal samples. X-ray diffraction…
Ionoluminescence (IL) and photoluminescence (PL) of trivalent erbium ions (Er3+) in Gd2O3 nanopowder host activated with Bi3+ ions has been studied in order to establish the link between changes in luminescent spectra and temperature of the…
Photoluminescence is observed at room temperature from phonon-assisted band-to-band emission in Si (1.067 eV peak) using unpatterned bulk p-type silicon wafer samples that were spin-coated with Er-doped (6 at. %) silica-gel films (0.13…
We have fabricated highly-luminescent samples with erbium-doped amorphous silicon sub-oxide (a-SiOx<Er>) layers on SiO2/Si substrates. The layers are designed to provide a resonance with large modal overlap with the active material and with…
We have studied the 1.5 $\mu$m photoluminescence (PL) from Er ions after annealing two different sample sets in the temperature range 500 °C to 1100 °C. The different sample sets were made by magnetron sputtering from composite…
Near band gap photoluminescence (PL) of hBN single crystal has been studied at cryogenic temperatures with synchrotron radiation excitation. The PL signal is dominated by the D-series previously assigned to excitons trapped on structural…