相关论文: Groove-rolling as an alternative process to fabric…
Recently the interest about Bi-2212 round wire superconductor for high magnetic field use has been enhancing despite the fact that an increase of the critical current is still needed to boost its successful use in such applications. Recent…
The first step towards high critical currents in Bi-2212 wires was the comprehension that the supercurrent is blocked over long lengths by filament-diameter bubbles grown during the melt stage, which cause expansion of the wire diameter and…
It is well known that longer Bi-2212 conductors have significantly lower critical current density (Jc) than shorter ones, and recently it has become clear that a major cause of this reduction is internal gas pressure generated during heat…
Bi-2212 round wire is made by the powder-in-tube technique. An unavoidable property of powder-in-tube conductors is that there is about 30% void space in the as-drawn wire. We have recently shown that the gas present in the as-drawn Bi-2212…
We report here that magnetic fields of almost 34 T, far above the upper 24 T limit of Nb3Sn, can be generated using a multifilament round wire conductor made of the high temperature cuprate superconductor Bi2Sr2CaCu2O8-x (Bi-2212). A…
Why Bi2Sr2CaCu2Ox (Bi2212) allows high critical current density Jc in round wires rather than only in the anisotropic tape form demanded by all other high temperature superconductors is important for future magnet applications. Here we…
Understanding what makes Bi$_2$Sr$_2$Ca$_1$Cu$_2$O$_x$ (Bi-2212) the only high critical current density ($J_c$), high temperature superconductor (HTS) capable of being made as a round wire (RW) is important intellectually because high $J_c$…
High engineering critical current density JE of >500 A/mm2 at 20 T and 4.2 K can be regularly achieved in Ag-sheathed multifilamentary Bi2Sr2CaCu2Ox (Bi-2212) round wire when the sample length is several centimeters. However, JE(20 T) in…
Significant insights for critical current density (Jc) improvement in Bi-2212 super- conductor wires can be obtained by an accurate analysis of the structural and mi- crostructural properties evolving during the so-called partial-melt…
Seven-core Ag/Fe sheathed Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires were produced by the ex situ powder-in-tube (PIT) method. The relationship between the cold-work deformation process and the superconducting properties of wires were…
Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires…
Bi-2212 is the only high-field, high-temperature superconductor (HTS) capable of reaching a critical current density $J_{\text{c}}$(16 T, 4.2 K) of 6500 $\mathrm{A\cdot mm^{-2}}$ in the highly desirable round wire (RW) form. However,…
The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…
The recently discovered iron-based superconductors with very high upper critical field and small anisotropy have been regarded as a potential candidate material for high field applications. However, enhancements of superconducting…
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of…
We fabricated (Ba,Na)Fe2As2 superconducting wires using the powder-in-tube method and hot isostatic pressing. By improving powder synthesis processes compared with previous studies, highly pure raw materials for the wire fabrication were…
Conductor insulation is one of the key components needed to make Ag-alloy clad Bi2Sr2CaCu2O8+x (Bi-2212/Ag) superconducting round wire (RW) successful for high field magnet applications as dielectric standoff and high winding current…
We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
We propose to use superconductor-magnet multi-layer structure to achieve high critical current density by invoking polaronic mechanism of pinning. The magnetic layers should have large magnetic susceptibility to enhance the coupling between…