Thorough mixing of the starting materials is the first step of a crystal growth procedure. This holds true for almost any standard technique, whereas the intentional separation of educts is considered to be restricted to a very limited…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
We report the single crystal growth of Ca(Fe1-xCox)2As2 (0 <= x <= 0.082) from Sn flux. The temperature-composition phase diagram is mapped out based on the magnetic susceptibility and electrical transport measurements. Phase diagram of…
We report a simple, reliable method to grow high quality BaFe$_{2-x}$Co$_x$As$_2$ single crystal samples without using any fluxing agent. The starting materials for the single crystal growth come from well-crystallized polycrystalline…
\alpha-Fe single crystals of rhombic dodecahedral habit were grown from a melt of Li$_{84}$N$_{12}$Fe$_{\sim 3}$. Crystals of several millimeter along a side form at temperatures around $T \approx 800^\circ$C. Upon further cooling the…
A description is given of the traveling solvent technique, which has been used for the crystal growth of both congruently and incongruently melting materials of many classes of intermetallic, chalcogenide, semiconductor and oxide materials.…
Single crystals of LiFeAs were successfully grown by a self-flux method using the cubic anvil high-pressure and high-temperature technique. The reaction took place in a closed boron nitride crucible at a pressure of 1 GPa and a temperature…
The growth of single crystals of MoS2 and WS2 by materials transport through a liquid salt flux made from a low melting mixture of NaCl and CsCl is described. The crystals are characterized by single crystal X-ray diffraction, which reveals…
Centimeter sized platelet single crystals of KFe2As2 were grown using a self-flux method. An encapsulation technique using commercial stainless steel container allowed the stable crystal growth lasting for more than 2 weeks. Ternary K-Fe-As…
ZnO bulk crystals can be grown by several methods. 1) From the gas phase, usually by chemical vapor transport. Such CVT crystals may have high chemical purity, as the growth is performed without contact to foreign material. The…
Superconductivity was discovered in a Ni0:05TaS2 single crystal. A Ni0:05TaS2 single crystal was successfully grown via the NaCl/KCl flux method. The obtained lattice constant c of Ni0:05TaS2 is 1.1999 nm, which is significantly smaller…
The high-pressure optical floating-zone method enables single crystal growth of the Pmnb high-temperature phase of Li2FeSiO4. The influence of growth conditions on crystal quality, phase homogeneity, and impurity formation in Li2FeSiO4 is…
Solution growth of single crystals from high temperature solutions often involves the separation of residual solution from the grown crystals. For many growths of intermetallic compounds, this separation has historically been achieved with…
BaTiS3, a quasi-1D complex chalcogenide, has gathered considerable scientific and technological interest due to its giant optical anisotropy and electronic phase transitions. However, the synthesis of high-quality BaTiS3 crystals,…
Up to now, investigation of physical properties of ternary and higher nitridometalates was severely hampered by challenges concerning phase purity and crystal size. Employing a modified lithium flux technique, we are now able to prepare…
We report a study on the crystal growth of the hexagonal manganites $R$MnO$_3$ ($R$ = Y, Lu, Ho, Er, and Tm) by using an optical floating-zone method. It was found that high-quality single crystals of $R$ = Y, Lu, and Ho could be easily…
Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline…
The bulk single crystals of $S = 1$ chain compound Ni(C$_3$H$_{10}$N$_2$)$_2$NO$_2$ClO$_4$ are grown by using a slow evaporation method at a constant temperature and a slow cooling method. It is found that the optimum condition of growing…
Single crystals of iridates are usually grown by a flux method well above the boiling point of the SrCl2 solvent. This leads to non-equilibrium growth conditions and dramatically shortens the lifetime of expensive Pt crucibles. Here, we…
We report the first single crystal growth of the correlated metal LaNiO3 using a high-pressure optical-image floating zone furnace. The crystals were studied using single crystal/powder x-ray diffraction, resistivity, specific heat, and…