Single crystals of Tl0.58Rb0.42Fe1.72Se2 are successfully grown with the superconducting transition temperatures Tconset=32K and Tczero=31.4K. The Hall coefficient exhibits a multi-band behavior, which is very similar to that of all other…

Superconductivity of Ca1-xLaxFe2As2 single crystals with various doping level were investigated via electromagnetic measurements for out-plane (H//c) and in-plane (H//ab) directions. Obvious double superconducting transitions, which can…

We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…

Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…

Anisotropic superconducting properties including the upper critical field Hc2, thermal activation energy U0, and critical current density Jc are systematically studied in a large Ca1-xLaxFeAs2 single crystal (x ~ 0.18). The obtained Hc2…

We successfully grew the high-quality single crystal of Rb$_{0.78}$Fe$_2$Se$_{1.78}$, which shows sharp superconducting transition in magnetic susceptibility and electrical resistivity. Resistivity measurements show the onset…

Using the self-flux technique we grew superconducting $(K_{1-z}Na_z)_{x}Fe_{2-y}Se_2$ (z = 0.3) single crystals. The EDX mapping revealed the uniform elements distribution on the crystal surface while the XRD measurements indicate that the…

The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…

Measurements of temperature-dependent in-plane resistivity, $\rho(T)$, were used to determine the upper critical field and its anisotropy in high quality single crystals of stoichiometric iron arsenide superconductor KFe$_2$As$_2$. The…

We have investigated the temperature dependence of the resistive upper critical fields ($\mu_{0}H_{\rm c2}(T)$) for an Fe$_{1.05}$Te$_{0.85}$Se$_{0.15}$ single crystal, which exhibit superconductivity at $T_{\rm c} \sim 14 K, in magnetic…

The transport and superconducting properties of Ba_{1-x}K_xFe_2As_2 single crystals with T_c = 31 K were studied. Both in-plane and out-of plane resistivity was measured by modified Montgomery method. The in-plane resistivity for all…

The anisotropic superconducting properties of single crystals of Cu0.07TiSe2 were studied by measurements of magnetization and electrical resistivity. TC is around 3.9 K, and the measured upper critical field (Hc2) values are ~1.25 T and…

We have determined the resistive upper critical field Hc2 for single crystals of the superconductor Fe1.11Te0.6Se0.4 using pulsed magnetic fields of up to 60T. A rather high zero-temperature upper critical field of mu0Hc2(0) approx 47T is…

In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…

Single crystals of Rb{0.8}Fe2Se2 are successfully synthesized with the superconducting transition temperatures T_c{onset}= 31 K and T_c{zero}= 28 K. A clear anomaly of resistivity was observed in the normal state at about 150 K, as found in…

Sizable single crystals of $BaFe_2As_2$ have been grown with self-flux method. The crystals are plate-like with c-axis perpendicular to the plane. The size can be as large as 3 x 5 x 0.2 $mm^3$. The resistivity anisotropy…

By using a hydrothermal method, we have successfully grown crystals of the newly discovered superconductor FeS, which has an isostructure of the iron based superconductor FeSe. The superconductivity appears at about 4.5K, as revealed by…

Quasi-single crystals (up to 2x2x1 mm3) of Na0.35CoO2.1.3H2O-superconductor have been grown. Magnetization M(H, T) and M(T, H) curves with magnetic field approximately parallel and perpendicular to c-axis indicates on large anisotropy,…

High-quality and sizable single crystals are crucial for studying the intrinsic properties of unconventional superconductors, which are lacking in the 1111 phase of the Fe-based superconductors. Here we report the successful growth of…

The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…