相关论文: Single crystal growth and characterization of the …
The magnetic and magnetotransport properties of metallic 1$T$-VTe$_{2}$ single crystals were investigated at temperatures from 1.3 to 300 K and in magnetic fields up to 35 T. Upon applying a high magnetic field, it is found that the…
By using high pressure and high temperature (3.7 GPa, 1120 $^{\circ}$C) synthesis technique, we have grown (Cu,C)Ba$_2$Ca$_3$Cu$_4$O$_{11+\delta}$ single crystals. X-ray diffraction, scanning electron microscopy, resistivity and…
We report both experimental and theoretical investigations of the physical properties of Ba$_\mathrm{2}$Mn$_\mathrm{2}$Sb$_\mathrm{2}$O single crystals. This material exhibits a hexagonal structure with lattice constants: a = 4.7029(15)…
The temperature dependence of resistivity, magnetization and electron-spin resonance of the $\alpha- MnS $ single crystal were measured in temperature range of $5 K < T < 550 K$. Magnetization hysteresis in applied magnetic field up to 0.7…
The magnetic properties of CoSi single crystals have been measured in a range of temperatures $T = 5.5 - 450$ K and magnetic field strengths $H \leq 11$ kOe. A comparison of the results for crystals grown in various laboratories allowed the…
In this study we examine the phase transitions in single crystals of [(CH3)2NH2]Co(HCOO)3], using magnetization and specific heat measurements as a function of temperature and magnetic field. Magnetisation measurements indicate a transition…
Single crystals of AlFe$_{2}$B$_{2}$ have been grown using the self flux growth method and then measured the structural properties, temperature and field dependent magnetization, and temperature dependent electrical resistivity at ambient…
We report the single crystal growth and characterization of EuIn$_2$, a magnetic topological semimetal candidate according to our density functional theory (DFT) calculations. We present results from electrical resistance, magnetization,…
Magnetization measurements and time-of-flight neutron powder-diffraction studies on the high-temperature (300--980 K) magnetism and crystal structure (321--1200 K) of a pulverized YCrO$_3$ single crystal have been performed.…
Single crystals of (Eu$_{1-x}$Ba$_x$)O have been grown in a molten barium-magnesium metal flux at temperatures up to 1000{\deg}C, producing single crystals of (Eu$_{1-x}$Ba$_x$)O with barium doping levels ranging from $x=0.03$ to $x=0.25$.…
The resistivity in the ferromagnetic state of flux-grown La_{2/3}(Pb,Ca)_{1/3}MnO_3 single crystals, measured in magnetic fields up to 7 T, reveals a strong quadratic temperature dependence at and above 50 K. At lower temperatures, this…
We report anisotropic dc magnetic susceptibility $\chi(T)$, electrical resistivity $\rho(T)$, and heat capacity $C(T)$ measurements on the single crystals of CaFe$_{2-x}$Co$_x$As$_2$ for $x$ = 0 and 0.06. Large sized single crystals were…
We report a study of magnetism and magnetic transitions of hexagonal ErMnO$_3$ single crystals by magnetization, specific heat and heat transport measurements. Magnetization data show that the $c$-axis magnetic field induces three magnetic…
The compound $Nb_{5-\delta}Te_4$ ($\delta=0.23$) with quasi-one-dimensional crystal structure undergoes a transition to superconductivity at $T_c$=0.6--0.9 K. Its electronic transport properties in the normal state are studied in the…
The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…
Extensive measurements of the magnetization of superconducting single crystal samples of Ba0.6K0.4BiO3} have been made using SQUID and cantilever force magnetometry at temperatures ranging between 1.3 and 350 K and in magnetic fields from…
Sizable single crystals of $BaFe_2As_2$ have been grown with self-flux method. The crystals are plate-like with c-axis perpendicular to the plane. The size can be as large as 3 x 5 x 0.2 $mm^3$. The resistivity anisotropy…
We studied single-crystals of the antiferromagnetic compound UNi0.5Sb2 (TN ~ 161 K) by means of measurements of magnetic susceptibility (chi), specific heat (Cp), and electrical resistivity (rho) at ambient pressure, and resistivity under…
The in-plane thermal conductivity K(T) of Zn-doped YBCO single crystals (YBCO:Zn) has been investigated in the temperature range from 5 to 250 K and in magnetic fields up to 30 kOe. The thermal conductivity decreases substantially with…
Single crystals of monoclinic La$_{5}$Co$_{2}$Ge$_{3}$ were grown using a self-flux method and were characterized by room-temperature powder X-ray diffraction, anisotropic temperature and field dependent magnetization, temperature dependent…