相关论文: Large critical current density improvement in Bi-2…
Bi2Sr2CaCu2O8+x (Bi-2212) superconducting long-length wires are mainly limited in obtaining high critical currents densities (JC) by the internal gas pressure generated during the heat treatment, which expands the wire diameter and…
The first step towards high critical currents in Bi-2212 wires was the comprehension that the supercurrent is blocked over long lengths by filament-diameter bubbles grown during the melt stage, which cause expansion of the wire diameter and…
Bi-2212 round wire is made by the powder-in-tube technique. An unavoidable property of powder-in-tube conductors is that there is about 30% void space in the as-drawn wire. We have recently shown that the gas present in the as-drawn Bi-2212…
It is well known that longer Bi-2212 conductors have significantly lower critical current density (Jc) than shorter ones, and recently it has become clear that a major cause of this reduction is internal gas pressure generated during heat…
Bi-2212 is the only high-field, high-temperature superconductor (HTS) capable of reaching a critical current density $J_{\text{c}}$(16 T, 4.2 K) of 6500 $\mathrm{A\cdot mm^{-2}}$ in the highly desirable round wire (RW) form. However,…
Understanding what makes Bi$_2$Sr$_2$Ca$_1$Cu$_2$O$_x$ (Bi-2212) the only high critical current density ($J_c$), high temperature superconductor (HTS) capable of being made as a round wire (RW) is important intellectually because high $J_c$…
Why Bi2Sr2CaCu2Ox (Bi2212) allows high critical current density Jc in round wires rather than only in the anisotropic tape form demanded by all other high temperature superconductors is important for future magnet applications. Here we…
Significant insights for critical current density (Jc) improvement in Bi-2212 super- conductor wires can be obtained by an accurate analysis of the structural and mi- crostructural properties evolving during the so-called partial-melt…
High engineering critical current density JE of >500 A/mm2 at 20 T and 4.2 K can be regularly achieved in Ag-sheathed multifilamentary Bi2Sr2CaCu2Ox (Bi-2212) round wire when the sample length is several centimeters. However, JE(20 T) in…
We propose to use superconductor-magnet multi-layer structure to achieve high critical current density by invoking polaronic mechanism of pinning. The magnetic layers should have large magnetic susceptibility to enhance the coupling between…
We fabricated (Ba,Na)Fe2As2 superconducting wires using the powder-in-tube method and hot isostatic pressing. By improving powder synthesis processes compared with previous studies, highly pure raw materials for the wire fabrication were…
Bi2Sr2CaCu2O8+x is the only cuprate superconductor that can be made into a round-wire conductor form with a high enough critical current density Jc for applications. Here we show that the Jc(5 T,4.2 K) of such Ag-sheathed filamentary wires…
The industrial manufacturing of the long-length iron-pnictide wires and tapes requires simple and low-cost technology. Although the transport critical current density of the FeAs-122 tapes has already achieved the practical application…
Large area arrays of through-thickness nanoscale pores have been milled into superconducting Nb thin films via a process utilizing anodized aluminum oxide thin film templates. These pores act as artificial flux pinning centers, increasing…
Seven-core Ag/Fe sheathed Sr0.6K0.4Fe2As2 (Sr-122) superconducting wires were produced by the ex situ powder-in-tube (PIT) method. The relationship between the cold-work deformation process and the superconducting properties of wires were…
We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
Iron-based superconductors have been considered to be very promising in high-field applications, for which multifilamentary wire and tape conductors with high mechanical strength are essential. In this work, 7-,19- and 114-filament…
We report here that magnetic fields of almost 34 T, far above the upper 24 T limit of Nb3Sn, can be generated using a multifilament round wire conductor made of the high temperature cuprate superconductor Bi2Sr2CaCu2O8-x (Bi-2212). A…
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The…
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the…