Temperature-dependent in-plane, $\rho_a(T)$, and inter-plane, $\rho_c(T)$, resistivities were measured for the iron-arsenide superconductor (Ba$_{1-x}$K$_x$)Fe $_2$As$_2$ over a broad doping range from parent compound to optimal doping…
Temperature-dependent inter-plane resistivity, $\rho _c(T)$, was measured in hole-doped iron-arsenide superconductor (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ over a doping range from parent compound to optimal doping $T_c\approx 38~K$, $0\leq x \leq…
Iron-arsenide superconductor Na$_{1-\delta}$FeAs is highly reactive with the environment. Due to the high mobility of Na ions, this reaction affects the entire bulk of the crystals and leads an to effective stoichiometry change. Here we use…
Large high-quality single crystals of hole-doped iron-based superconductor (Ba$_{1-x}$K$_x$)Fe$_2$As$_2$ were grown over a broad composition range $0.22 \leq x \leq 1$ by inverted temperature gradient method. We found that high soaking…
Temperature-dependent inter-plane resistivity, $\rho_c(T)$, was measured systematically as a function of transition metal substitution in the iron-arsenide superconductors Ba(Fe$_{1-x}$T$_x$)$_2$As$_2$, $T$= Ni, Pd, Rh. The data are…
We measured the in-plane resistivity anisotropy in the underdoped Ca$_{1-x}$Na$_x$Fe$_2$As$_2$ single crystals. The anisotropy (indicated by $\rho_{\rm b} - \rho_{\rm a}$) appears below a temperature well above magnetic transition…
The London penetration depth was measured in single crystals of self-doped Na$_{1-\delta}$FeAs (from under - to optimal - doping, $T_c$ from 14 to 27 K) and electron-doped Na(Fe$_{1-x}$Co$_{x}$)As with $x$ ranging from undoped, $x=0$ to…
We measured the resistivity and magnetic susceptibility to map out the phase diagram of single crystalline NaFe$_{1-x}$Co$_x$As. Replacement of Fe by Co suppresses both the structural and magnetic transition, while enhances the…
Temperature-dependent inter-plane resistivity, $\rho _c(T)$, was used to characterise the normal state of the iron-arsenide superconductor Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ over a broad doping range $0\leq x<0.50$. The data were compared with…
To elucidate how the temperature dependence of the resistivity anisotropy of the cuprate superconductors changes with hole doping, both the in-plane and the out-of-plane resistivities (\rho_{ab} and \rho_{c}) are measured in a series of…
We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single…
Superconductivity was recently observed in the iron-arsenic-based compounds with a superconducting transition temperature (Tc) as high as 56K [1-7], naturally raising comparisons with the high Tc copper oxides. The copper oxides have…
We report a doping, magnetic field and low-temperature dependent study of the specific heat of the iron-arsenide Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$ at under (x=0.045), optimal (x=0.08) and overdoped (x=0.103 and 0.105) regimes. By…
In iron pnictides, high temperature superconductivity emerges after suppressing antiferromagnetism by doping. Here we show that antiferromagnetism in Ca$_{1-x}$La$_x$FeAs$_2$ is robust against and even enhanced by doping. Using…
Temperature-dependent inter-plane resistivity, $\rho_c(T)$, was measured for the iron-based superconductor BaFe$_2$(As$_{1-x}$P$_x$)$_2$ over a broad isoelectron phosphorus substitution range from $x$=0 to $x$=0.60, from non-superconducting…
High temperature superconductivity emerges in the vicinity of competing strongly correlated phases. In the iron-based superconductor $Ba(Fe_{1-x}Co_{x})_{2}As_{2}$, the superconducting state shares the composition-temperature phase diagram…
Single crystalline samples of Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ with $x < 0.12$ have been grown and characterized via microscopic, thermodynamic and transport measurements. With increasing Co substitution, the thermodynamic and transport…
The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…
The temperature and magnetic field dependence of the in-plane thermal conductivity $\kappa$ of the iron-arsenide superconductor Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ was measured down to $T \simeq 50$ mK and up to $H = 15$ T as a function of Co…
The upper critical field ($H_{c2}$) in superconducting BaFe$_{2-x}$Ni$_{x}$As$_2$ single crystals has been determined by magnetotransport measurements down to 0.6 K over the whole superconducting dome with $0.065 \leqslant x \leqslant…