相关论文: Superconductivity at 32 K in single crystal Rb$_{0…
We successfully grew the high-quality single crystals of $A_{x}$Fe$_2$Se$_2$ ($A$ = K and Cs) by self-flux method. Sharp superconducting transition was observed for both types of crystals. The crystals show the onset superconducting…
Single crystals of Tl0.58Rb0.42Fe1.72Se2 are successfully grown with the superconducting transition temperatures Tconset=32K and Tczero=31.4K. The Hall coefficient exhibits a multi-band behavior, which is very similar to that of all other…
We report the crystal growth and structural, magnetic, conductivity, and specific heat investigations of Rb(1-x)Fe(2-y)Se2 single crystals with varying stoichiometry prepared by self-flux and Bridgman methods. The system exhibits a strongly…
We have determined the resistive upper critical field Hc2 for single crystals of the superconductor Fe1.11Te0.6Se0.4 using pulsed magnetic fields of up to 60T. A rather high zero-temperature upper critical field of mu0Hc2(0) approx 47T is…
We synthesized the new Fe-based superconductor K0.8Fe2Se2 single crystals. The obtained single crystal exhibited a sharp superconducting transition, and the onset and zero-resistivity temperature was estimated to be 33 and 31.8 K,…
Single crystals of Rb{0.8}Fe2Se2 are successfully synthesized with the superconducting transition temperatures T_c{onset}= 31 K and T_c{zero}= 28 K. A clear anomaly of resistivity was observed in the normal state at about 150 K, as found in…
We report resistivity measurements performed on KFe$_2$As$_2$ single crystals down to $T$ = 0.3 K and in magnetic fields up to 17.5 T. The in-plane resistivity vs. $T$ curve has a convex shape down to $\sim$50 K and shows a $T^2$ dependence…
Measurements of temperature-dependent in-plane resistivity, $\rho(T)$, were used to determine the upper critical field and its anisotropy in high quality single crystals of stoichiometric iron arsenide superconductor KFe$_2$As$_2$. The…
Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…
We measure the resistivity and magnetic susceptibility in the temperature range from 5 K to 600 K for the single crystals $A$Fe$_{2-y}$Se$_2$ ($A$ = K$_{0.8}$, Rb$_{0.8}$, Cs$_{0.8}$, Tl$_{0.5}$K$_{0.3}$ and Tl$_{0.4}$Rb$_{0.4}$). A sharp…
Single crystals of Ba_{1-x}Rb_{x}Fe_2As_2 with x=0.05-0.1 have been grown from Sn flux and are bulk superconductors with T_c up to 23 K. The crystal structure was determined by X-ray diffraction analysis, and Sn is found to be incorporated…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
We report the in-plane resistivity and magnetic susceptibility of the layered cobalt oxide Na$_{0.35}$CoO$_{2}{\cdot}1.3$H$_{2}$O single crystal. The temperature dependence of the resistivity shows metallic behavior from room temperature to…
CsCa$_2$Fe$_4$As$_4$F$_2$ is a newly discovered iron-based superconductor with $T_\mathrm{c}\sim$ 30 K containing double Fe$_2$As$_2$ layers that are separated by insulating Ca$_2$F$_2$ spacer layers. Here we report the transport and…
We present a detailed study of the electrical transport properties of a recently discovered iron-based superconductor: Sm$_4$Fe$_2$As$_2$Te$_{0.72}$O$_{2.8}$F$_{1.2}$. We followed the temperature dependence of the upper critical field by…
We have investigated the temperature dependence of the resistive upper critical fields ($\mu_{0}H_{\rm c2}(T)$) for an Fe$_{1.05}$Te$_{0.85}$Se$_{0.15}$ single crystal, which exhibit superconductivity at $T_{\rm c} \sim 14 K, in magnetic…
Using the self-flux technique we grew superconducting $(K_{1-z}Na_z)_{x}Fe_{2-y}Se_2$ (z = 0.3) single crystals. The EDX mapping revealed the uniform elements distribution on the crystal surface while the XRD measurements indicate that the…
The anisotropic superconducting properties of a Rb(x)Fe(2-y)Se(2) single crystal with transition temperature 32 K were investigated by means of SQUID and torque magnetometry, probing the effective magnetic penetration depth and the magnetic…
The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature…
Single crystals of the compound LaFePO were prepared using a flux growth technique at high temperatures. Electrical resistivity measurements reveal metallic behavior and a resistive transition to the superconducting state at a critical…