We report a simple, reliable method to grow high quality BaFe$_{2-x}$Co$_x$As$_2$ single crystal samples without using any fluxing agent. The starting materials for the single crystal growth come from well-crystallized polycrystalline…
Single crystals of A$_{1-x}$K$_x$Fe$_2$As$_2$ (A=Ba, Sr) with high quality have been grown successfully by FeAs self-flux method. The samples have sizes up to 4 mm with flat and shiny surfaces. The X-ray diffraction patterns suggest that…
Superconducting single crystals of SmFeAsO$_{1-x}$ without fluorine doping were grown at a pressure of 3.3 GPa and a temperature of 1350-1450 $^\circ$C by using the self-flux method. Plate-like single crystals of a few-150 $\mu$m in their…
Centimeter sized platelet single crystals of KFe2As2 were grown using a self-flux method. An encapsulation technique using commercial stainless steel container allowed the stable crystal growth lasting for more than 2 weeks. Ternary K-Fe-As…
We report successful growth of flux free large single crystals of superconducting FeSe1/2Te1/2 with typical dimensions of up to few cm. The AC and DC magnetic measurements revealed the superconducting transition temperature (Tc) value of…
In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are…
To prevent the loss of K in growing single crystals of Ba1-x Kx Fe2 As2 we developed a rapid heating Sn-flux method. Large single crystals with the optimal superconducting transition temperature TC about 38K were obtained and their…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single…
A new approach to grow FeSe1-xTex single crystals with optical zone-melting technique was successfully employed. Crystals with actual composition 0.4 < x < 1.0 all show high crystallinity with no phase separation. The ability to visually…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition…
"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the…
A flux-free solution to the growth of large and composition homogeneous superconducting FeSe crystal is reported for the first time, which is based on the traveling-solvent floating-zone technique. The size of the crystal samples prepared…
Co-doped iron arsenic single crystal of BaFe1.87Co0.13As2 with dimension up to 20 x 10 x 2 mm3 were grown by a nucleation pole: an alumina stick served as nucleation center during growth. The high quality of crystalline was illustrated by…
Single crystals of SmFeAsO1-xFy of a size up to 120 micrometers have been grown from NaCl/KCl flux at a pressure of 30 kbar and temperature of 1350-1450 C using the cubic anvil high-pressure technique. The superconducting transition…
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l)…
Measurements of the anisotropic properties of single crystals play a crucial role in probing the physics of new materials. Determining a growth protocol that yields suitable high-quality single crystals can be particularly challenging for…
Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using…
High-quality Bi$_{2+x}$Sr$_{2-x}$CuO$_{6+\delta}$(0$<$x$\leq$0.5) single crystals have been grown successfully using the travelling-solvent floating-zone(TSFZ) technique. The samples with $x >$ 0.05 are in the underdoped level. The…
We report the single crystal growth of Ca(Fe1-xCox)2As2 (0 <= x <= 0.082) from Sn flux. The temperature-composition phase diagram is mapped out based on the magnetic susceptibility and electrical transport measurements. Phase diagram of…