相关论文: Superconductivity at 56 K in Samarium-doped SrFeAs…

A suppression of superconductivity in the late rare earth RFeAsO1-xFx materials is reported. The maximum critical temperature (Tc) decreases from 51 K for R = Tb to 36 K for HoFeAsO0.9F0.1, which has been synthesised under 10 GPa pressure.…

The fluorine-doped rare-earth iron oxyarsenides, REFeAsO1-xFx (RE =rare earth) have recently emerged as a new family of high-temperature superconductors with transition temperatures (Tc) as high as 55 K (refs 1-4). Early work has provided…

We report the realization of superconductivity by 5d element Ir doping in LaFeAsO, a prototype parent compound of high-temperature iron based superconductors. X-ray diffraction patterns indicate that the material has formed the…

We discover superconductivity in alkali-earth metals doped phenanthrene. The superconducting critical temperatures \emph{T}$_c$ are 5.6 K and 5.4 K for Sr$_{1.5}$phenanthrene and Ba$_{1.5}$phenanthrene, respectively. The shielding fraction…

The superconductor Sr4V2O6Fe2As2 with transition temperature at 37.2 K has been fabricated. It has a layered structure with the space group of p4/nmm, and with the lattice constants a = 3.9296Aand c = 15.6732A. The observed large…

Study of superconductivity in layered iron-based materials was initiated in 2006 by Hosono's group, and boosted in 2008 by the superconducting transition temperature, Tc, of 26 K in LaFeAsO1-xFx. Since then, enormous researches have been…

Following the discovery of superconductivity in an iron-based arsenide LaO1-xFxFeAs with a superconducting transition temperature (Tc) of 26 K[1], Tc was pushed up surprisingly to above 40 K by either applying pressure[2] or replacing La…

Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…

By substituting the Fe with the 4d and 5d-transition metals Rh, Ir and Pd in SrFe_2As_2, we have successfully synthesized a series of superconductors SrFe_{2-x}M_xAs_2 (M = Rh, Ir and Pd) and explored the phase diagrams of them. The…

In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…

By doping Rh to the Fe sites in SrFe2As2, superconductivity is induced when the antiferromagnetic (AF) order is suppressed. The maximum superconducting transition temperature was found at about 22 K with the doping level of x = 0.25. It is…

Polycrystalline Sr1-xNdxFeAsF samples were prepared at various Nd-doping levels using both a stoichiometric mixture of the starting materials and in slight excess amounts of FeAs. Susceptibility and resistivity of the samples were studied…

The new quaternary iron arsenide-fluoride SrFeAsF with the tetragonal ZrCuSiAs-type structure was synthesized and the crystal structure was determined by X-ray powder diffraction (P4/nmm, a = 399.30(1), c = 895.46(1) pm). SrFeAsF undergoes…

We report on the synthesis and microstructural studies of fluorine based iron doped superconductors. We have successfully synthesized the fluorine based new superconducting material LaO1-xFxFeAs by choosing comparatively lower temperature…

We report resistivity measurement under pressure in single crystals of SrFe_2As_2, which is one of the parent materials of Fe-based superconductors. The structural and antiferromagnetic (AFM) transition of T_0 = 198 K at ambient pressure is…

In this paper, nominal compositions of NdFeAsO0.8F0.2, NdFeAs0.95Sb0.05O0.8F0.2 and NdFeAs0.95P0.05O0.8F0.2 were prepared by one step solid state reaction method. The structural, electrical and morphological properties of samples were…

Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1-xKxFe2As2, which is the maximum found thus far among the 122 phases.…

EuFe2As2 is a member of the ternary iron arsenide family. Similar to BaFe2As2 and SrFe2As2, EuFe2As2 exhibits a clear anomaly in resistivity near 200 K. It suggests that EuFe2As2 is another promising parent compound in which…

We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…

Fluoride-doped iron-based oxypnictides containing rare-earth gadolinium (GdFeAsO0.8F0.2) and co-doping with yttrium (Gd0.8Y0.2FeAsO0.8F0.2) have been prepared via conventional solid state reaction at ambient pressure. The non-yttrium…