Related papers: Improved superconducting properties of MgB2
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…
The critical current density (Jc) of hot isostatic pressed (HIPed) MgB2 wires, measured by d.c. transport and magnetization, is compared with that of similar wires annealed at ambient pressure. The HIPed wires have a higher Jc than the…
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a…
Here we report a systematic study of superconductive properties of mono-filamentary MgB2-based wires, manufactured with different filling technique. A detailed comparison of the influence of filling technique and final heat treatment on…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated by transport, ac susceptibility and dc magnetization measurements in magnetic fields up to 16 T covering a temperature…
The bulk upper critical field H_{c2}(T) of superconducting MgB_2 and its anisotropy are established by analyzing experimental data on the temperature and magnetic field dependences of the ab-plane thermal conductivity of a…
Recently, an extremely high superconducting temperature (Tc) of ~200 K has been reported in the sulfur hydride system above 100 GPa. This result is supported by theoretical predictions and verified experimentally. The crystal structure of…
High quality bulk MgB2 exhibit a structure of voids and agglomeration of crystals on different length-scales. Because of this, the superconducting currents percolate between the voids in the ensuing structure. Magnetic measurements reveal…
MgB2 is a promising superconductor for important large-scale applications for both high field magnets and cryocooler-cooled magnet operated at temperatures around 20 K. In this work, by utilizing C60 as a viable alternative dopant, we…
We report specific heat measurements in neutron irradiated MgB2 samples, for which the critical temperature has been suppressed down to 8.5 K, but the superconducting transition remains extremely sharp, indicative of a defect structure…
Measurements of the superconducting transition temperature Tc have been performed by the inductive method on MgB2 at pressures up to 28 GPa. Tc decreases with applied pressure, exhibiting a cusp at about 9 GPa. We interpret the appearance…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
A series of doping experiments are reported for MgB2 conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition(CVD) methods. Undoped MgB2 samples prepared from CVD prepared fibers consistently give…
The heat-capacity and magnetization measurements under high pressure have been carried out in a ferromagnetic superconductor UGe$_2$. Both measurements were done using a same pressure cell in order to obtain both data for one pressure.…
In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…
Recently it was discovered that, under elevated pressures, MoB$_2$ exhibits superconductivity at a critical temperature, $T_c$, as high as 32 K. The superconductivity appears to develop following a pressure-induced structural transition…
Electrical resistivity experiments show superconductivity at $T_c = 1.1\,$K in a high-quality single crystal of trigonal $\gamma$-PtBi$_2$, with an enhanced critical magnetic field $\mu_0H_{c2}(0) \gtrsim 1.5\,$Tesla and a low critical…
Cryogenic scanning tunneling microscopy and magnetization measurements were used to study the superconducting properties of MgB_2. The magnetization measurements show a sharp superconductor transition onset at T_c = 38.5 K, in agreement…
The recent surprising discovery of superconductivity with critical temperature $T_c$ = 32 K in MoB$_2$ above 70 GPa has led to the search for related materials that may superconduct at similarly high $T_c$ values and lower pressures. We…
The recently-discovered MgB2 super-conductor has a transition temperature Tc approaching 40K, placing it intermediate between the families of low and high temperature super-conductors (LTS and HTS). In practical applications,…