Related papers: Improved superconducting properties of MgB2
The MgB2 coated superconducting tapes have been fabricated on textured Cu (0 0 1) and polycrystalline Hastelloy tapes using coated conductor technique, which has been developed for the second generation high temperature superconducting…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…
Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…
The pressure effect on the superconducting transition temperature of MgB2 has been determined using gas pressure up to 1 GPa. The transition temperature Tc was found to decrease linearly at a constant rate over the whole pressure range. The…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
Recently co-existence of the ferromagnetism and superconductivity was reported in the high-pressure region (1.0-1.6 GPa) in UGe$_2$. We performed the heat capacity measurement on UGe$_2$ under high pressure. At 1.13 GPa, we found a peak…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…
Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
A MgB2 superconducting tape has been successfully prepared by a new way of boron diffusion into Mg tape. This tape superconductor has a Tc of 39 K with a sharp transition width of 0.4 K, high bulk critical current density jc of 6.7*10^5…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
We report phase formation, and detailed study of magnetization and resistivity under magnetic field of MgB2 polycrystalline bulk samples prepared by Fe-tube encapsulated and vacuum (10-5 torr) annealed (750 0C) route. Zero-field-cooled…
The dependence of Tc on nearly hydrostatic pressure has been measured for an isotopically pure (11B) MgB2 sample in a helium-loaded diamond-anvil-cell to nearly 20 GPa. Tc decreases monotonically with pressure from 39.1 K at ambient…
Far-infrared reflectivity studies on the polycrystalline intermetallic compound MgB_2 with a superconducting transition temperature T_c=39 K were performed at temperatures 20 K to 300 K. We observe a significant raise of the…
The discovery of superconductivity at 39 K in MgB2[1] raises many issues. One of the central questions is whether this new superconductor resembles a high-temperature-cuprate superconductor or a low-temperature metallic superconductor in…
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical…
Precursor MgB2 thin films were prepared on sapphire substrates by magnetron sputtering. Influence of ex-situ annealing process on superconducting MgB2 thin films roughness is discussed. Optimized annealing process of MgB precursor thin…
We synthesized polycrystalline MgB2 from a stoichiometric mixture of Mg and the 11 B isotope under different conditions. All the samples showed bulk superconductivity with Tc = 38~39 K. The samples containing the least amount of unreacted…